MgCl2·6H2O‐based titanium catalyst for propylene polymerization: Effect of polymerization parameters

A supported titanium catalyst was prepared by using MgCl2·6H2O as a precursor for generating an active support. The performance of such catalyst was evaluated for propylene polymerization in conjunction with triethylaluminium as cocatalyst and dimethoxydiphenylsilane as an external Lewis base. The efficiency of the catalyst system is dependent on the polymerization parameters such as time, temperature and monomer pressure. The variation in the concentration of hydrogen used as a chain transfer agent alters the performance of the catalyst system and molecular weight characteristics of polypropylene. The morphology of polymer particles is of globular type and is not affected by the variation in the melt flow characteristics of the polymer. Ausgehend von MgCl2·6H2O als Vorstufe wurde ein titanhaltiger Tragerkatalysator hergestellt. Zusammen mit Triethylaluminium als Cokatalysator und Dimethoxydiphenylsilan als externer Lewis-Saure wurde das Verhalten dieses Ktalysators bei der Polymerisation von Propylen untersucht. Die Effektivitat des Ktalysatorsystems hangt von den Polymerisationsparametern Zeit, Temperatur und Monomerdruck ab. Eine Variation der Konzentration von als Kettenubertrager verwendetem Wasserstoff bewirkt eine Anderung der Katalysatoreigenschaften und der Molekulargewichtscharakteristik des Polypropylens. Die Polymerpartikel weisen eine globulare Morphologie auf, die nicht von Anderungen der Schmelzfluseigenschaften beeinflust wird.