Truncated Edge Cuprous Oxide Cube Architecture for Reduction of Nitrophenols

ABSTRACT Truncated cubic Cu-oxide nanocrystals with edge lengths of ca. 600 nm were prepared employing the low-cost copper (II) chloride as the precursor. XRD revealed that the truncated cubic Cu-oxide nanocrystals are present in both the CuI and Cu0 state. XPS characterisation gives insight into the amount of each state present in the as-prepared, oxidised, reduced and recovered catalyst species. The catalytic activity of the truncated cubic Cu-oxide nanocrystals was tested for the reduction of nitrophenols using NaBH4. After one catalytic cycle of the reduction of 4-nitrophenol, the activity almost halved. The SEM images revealed that the recovered catalyst showed some disfigurement of the structure, and XPS confirmed the reduction of the CuI to metallic Cu0. Keywords: Cu-oxide, truncated cubic nanocrystal, nitrophenol, catalysis, X-ray photoelectron spectroscopy.