The Potentialities of Raman and XPS Techniques to Evaluate the Corrosion Products Formed on the 2198-T851 Aluminium Alloy Exposed to Sodium Chloride Solution

The aerospace industry is constantly looking for innovative materials that exhibit good mechanical and corrosion properties. The 2198-T851 (Al-Cu-Li) alloy was developed to replace the conventional Al-Cu-Mg in aircraft structures. Despite the usefulness of the 2198-T851 alloy, its performance may be affected when subjected to an aggressive medium containing chloride ions. The deposition of Nb 2 O 5 coatings by using the reactive sputtering technique on the 2198-T851 alloy surface appears as a powerful tool to improve the corrosion resistance of this material. Recently, groundbreaking research findings have demonstrated the positive effect of Nb 2 O 5 coatings on corrosion protection of alloy 2198-T851. However, the corrosion products originated from the 2198-T851 aluminium alloy are poorly understood. The use of Raman spectroscopy and XPS techniques may help to shed some light on the corrosion products of 2198-T851 alloy. Results demonstrated the corrosion products are mainly composed by CuCl 2 x H 2 O, CuCl, Cu 2 Cl(OH) 3 , Al(OH) 3 , and AlO(OH).