Metal dusting of nickel-based alloys

The carburization behavior of nine commercial nickel-based alloys and four iron-nickel-chromium alloys was investigated at 650°C in a carburizing carbon monoxide (CO)-H 2 hydrogen oxide (H 2 O) gas with a carbon activity (a c ) of a c > 1. The iron-nickel-chromium alloys suffered severe metal dusting after a very short test period. Nickel-based alloys were generally less susceptible to metal dusting than iron-based alloys. Nickel-based alloys with chromium concentrations of 25% and above, on the other hand, showed no significant evidence of metal dusting even after 10,000 h of exposure. It was found that these alloys were protected against metal dusting by the formation of a dense, self-healing chromia scale, which prevented the penetration of carbon into the base metal.