Enhanced thermal and dielectric properties of porous thin films of graphene, conjugated terpolymer of pyrene/thiophene/heptaldehyde, and polyvinylidene difluoride alloys

We have developed conductive, lightweight, and porous composite of polyvinylidene difluoride by blending with synthesized conjugated terpolymer and graphene for conductive polymer composite applications. The new conjugated terpolymer designated as PEPy-TP is synthesized from 3,4-ethylenedioxythiophene, 1-pyrenecarboxzaldehyde, and heptaldehyde through friedel craft reaction. The synthesized terpolymer PEPy-TP have been blended with polyvinylidene difluoride and graphene nanosheets to form porous composite and has been characterized using XRD, TGA, TG-DSC, DTA, DTG, SEM, EDX, and Dielectric spectroscopy. The porous composite is comprised of varying weight percentages of (1, 3, and 5%) of GNS and 10 wt% PEPy-TP in PVDF. The thermal studies on the porous composites indicated that the decomposition occurred at a temperature around 270 and 470 °C corresponds to the PEPy-TP and PVDF/PEPy-TP/GNS (1, 3, and 5%), respectively. The EDX spectrum of neat PEPy-TP polymer and their porous composites of PVDF/PEPy-TP/GNS (1, 3, and 5%) result clearly shows the presence of all elements, such as C, O, S, and F with an atomic weight percentage also. The PVDF/PEPy-TP/5% GNS porous composites having a tremendous electrical conductivity and the dielectric constant value is 56 at 1 MHz and their conductivity of this polymer porous composites value is determined to be 4.9 × 10⁻⁶ S/cm at 100 kHz, respectively.