阳极电泳沉积在镍基合金上制备YSZ涂层

IF 0.7 4区工程技术 Q4 CHEMISTRY, APPLIED

Polish Journal of Chemical Technology Pub Date : 2023-02-18 DOI:10.2478/pjct-2023-0002

Binxia Yuan, Tianzhong Chen, Yongzhi Shang, Xue Haibo, Li Min

{"title":"阳极电泳沉积在镍基合金上制备YSZ涂层","authors":"Binxia Yuan, Tianzhong Chen, Yongzhi Shang, Xue Haibo, Li Min","doi":"10.2478/pjct-2023-0002","DOIUrl":null,"url":null,"abstract":"Abstract In the paper, YSZ coatings were prepared on nickel-based alloy substrates by anodic electrophoretic deposition. The YSZ suspension solution was obtained under stirring and ultrasonic treatment, in which the anhydrous ethanol and acetylacetone were used as the dispersion medium and ammonium polyacrylate was used as the dispersant of the suspension. The effects of different deposition voltage and deposition time on YSZ coating were investigated. Meantime, the microstructure of the coating surface was observed by metallographic microscope. It was found that the high-quality YSZ coating could be obtained by deposition at 60 V for 2–3 min. Finally, the effect of sintering temperature on coating quality was investigated by X-ray diffractometer and scanning electron microscopy. The results showed that the YSZ coating bonded closely with the substrate after sintering at 1200 oC, and the porosity of the YSZ coating increased after sintering","PeriodicalId":20324,"journal":{"name":"Polish Journal of Chemical Technology","volume":"25 1","pages":"8 - 11"},"PeriodicalIF":0.7000,"publicationDate":"2023-02-18","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Fabrication of YSZ coatings on nickel-based alloys by anodic electrophoretic deposition\",\"authors\":\"Binxia Yuan, Tianzhong Chen, Yongzhi Shang, Xue Haibo, Li Min\",\"doi\":\"10.2478/pjct-2023-0002\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Abstract In the paper, YSZ coatings were prepared on nickel-based alloy substrates by anodic electrophoretic deposition. The YSZ suspension solution was obtained under stirring and ultrasonic treatment, in which the anhydrous ethanol and acetylacetone were used as the dispersion medium and ammonium polyacrylate was used as the dispersant of the suspension. The effects of different deposition voltage and deposition time on YSZ coating were investigated. Meantime, the microstructure of the coating surface was observed by metallographic microscope. It was found that the high-quality YSZ coating could be obtained by deposition at 60 V for 2–3 min. Finally, the effect of sintering temperature on coating quality was investigated by X-ray diffractometer and scanning electron microscopy. The results showed that the YSZ coating bonded closely with the substrate after sintering at 1200 oC, and the porosity of the YSZ coating increased after sintering\",\"PeriodicalId\":20324,\"journal\":{\"name\":\"Polish Journal of Chemical Technology\",\"volume\":\"25 1\",\"pages\":\"8 - 11\"},\"PeriodicalIF\":0.7000,\"publicationDate\":\"2023-02-18\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Polish Journal of Chemical Technology\",\"FirstCategoryId\":\"5\",\"ListUrlMain\":\"https://doi.org/10.2478/pjct-2023-0002\",\"RegionNum\":4,\"RegionCategory\":\"工程技术\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"CHEMISTRY, APPLIED\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Polish Journal of Chemical Technology","FirstCategoryId":"5","ListUrlMain":"https://doi.org/10.2478/pjct-2023-0002","RegionNum":4,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"CHEMISTRY, APPLIED","Score":null,"Total":0}

引用次数: 0

摘要

摘要采用阳极电泳法在镍基合金基体上制备了YSZ涂层。以无水乙醇和乙酰丙酮为分散介质，聚丙烯酸铵为分散剂，在搅拌和超声处理下得到YSZ悬浮液。研究了不同沉积电压和沉积时间对YSZ涂层性能的影响。同时，用金相显微镜观察了涂层表面的微观结构。研究发现，在60 V下沉积2–3分钟可以获得高质量的YSZ涂层。最后，通过X射线衍射仪和扫描电子显微镜研究了烧结温度对涂层质量的影响。结果表明，在1200℃烧结后，YSZ涂层与基体结合紧密，烧结后YSZ涂层的孔隙率增加

本文章由计算机程序翻译，如有差异，请以英文原文为准。

查看原文本刊更多论文

Fabrication of YSZ coatings on nickel-based alloys by anodic electrophoretic deposition

Abstract In the paper, YSZ coatings were prepared on nickel-based alloy substrates by anodic electrophoretic deposition. The YSZ suspension solution was obtained under stirring and ultrasonic treatment, in which the anhydrous ethanol and acetylacetone were used as the dispersion medium and ammonium polyacrylate was used as the dispersant of the suspension. The effects of different deposition voltage and deposition time on YSZ coating were investigated. Meantime, the microstructure of the coating surface was observed by metallographic microscope. It was found that the high-quality YSZ coating could be obtained by deposition at 60 V for 2–3 min. Finally, the effect of sintering temperature on coating quality was investigated by X-ray diffractometer and scanning electron microscopy. The results showed that the YSZ coating bonded closely with the substrate after sintering at 1200 oC, and the porosity of the YSZ coating increased after sintering

求助全文

通过发布文献求助，成功后即可免费获取论文全文。去求助

来源期刊

Polish Journal of Chemical Technology CHEMISTRY, APPLIED-ENGINEERING, CHEMICAL

CiteScore

1.70

自引率

10.00%

发文量

审稿时长

4.5 months

期刊介绍： Polish Journal of Chemical Technology is a peer-reviewed, international journal devoted to fundamental and applied chemistry, as well as chemical engineering and biotechnology research. It has a very broad scope but favors interdisciplinary research that bring chemical technology together with other disciplines. All authors receive very fast and comprehensive peer-review. Additionally, every published article is promoted to researchers working in the same field.