{"title":"不同粘接材料表面粗糙度对粘接强度的影响","authors":"S. Budhe, A. Ghumatkar, N. Birajdar, M. D. Banea","doi":"10.1186/s40563-015-0050-4","DOIUrl":null,"url":null,"abstract":"<p>In this paper, an experimental study on the effect of surface roughness of different adherend material on adhesive bond strength was carried out. The adherend material used was aluminium AA6061 and wood in the form of sheet, and the adhesive was an epoxy resin. Different surface roughness obtained by mechanical abrasion using an emery paper and sand paper for aluminium and wood adherend samples respectively. Single strap joints were tested at room temperature. Results showed that there is clear dependency observed in between the adhesive bond strength and surface roughness of both wood and aluminium adherend joints. Optimum surface roughness values were obtained in the range of R<sub>a</sub>?=?1.68?±?0.14?μm and R<sub>a</sub>?=?1.64?±?0.2?μm for the aluminium and wood adherend joints respectively. Surface roughness along with the adhered material parameters should be considered during design stage of adhesively bonded joints.</p>","PeriodicalId":464,"journal":{"name":"Applied Adhesion Science","volume":"3 1","pages":""},"PeriodicalIF":1.6800,"publicationDate":"2015-12-14","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://sci-hub-pdf.com/10.1186/s40563-015-0050-4","citationCount":"81","resultStr":"{\"title\":\"Effect of surface roughness using different adherend materials on the adhesive bond strength\",\"authors\":\"S. Budhe, A. Ghumatkar, N. Birajdar, M. D. Banea\",\"doi\":\"10.1186/s40563-015-0050-4\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p>In this paper, an experimental study on the effect of surface roughness of different adherend material on adhesive bond strength was carried out. The adherend material used was aluminium AA6061 and wood in the form of sheet, and the adhesive was an epoxy resin. Different surface roughness obtained by mechanical abrasion using an emery paper and sand paper for aluminium and wood adherend samples respectively. Single strap joints were tested at room temperature. Results showed that there is clear dependency observed in between the adhesive bond strength and surface roughness of both wood and aluminium adherend joints. Optimum surface roughness values were obtained in the range of R<sub>a</sub>?=?1.68?±?0.14?μm and R<sub>a</sub>?=?1.64?±?0.2?μm for the aluminium and wood adherend joints respectively. Surface roughness along with the adhered material parameters should be considered during design stage of adhesively bonded joints.</p>\",\"PeriodicalId\":464,\"journal\":{\"name\":\"Applied Adhesion Science\",\"volume\":\"3 1\",\"pages\":\"\"},\"PeriodicalIF\":1.6800,\"publicationDate\":\"2015-12-14\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://sci-hub-pdf.com/10.1186/s40563-015-0050-4\",\"citationCount\":\"81\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Applied Adhesion Science\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://link.springer.com/article/10.1186/s40563-015-0050-4\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"Dentistry\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Applied Adhesion Science","FirstCategoryId":"1085","ListUrlMain":"https://link.springer.com/article/10.1186/s40563-015-0050-4","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"Dentistry","Score":null,"Total":0}
引用次数: 81
摘要
本文对不同粘结材料的表面粗糙度对粘结强度的影响进行了实验研究。粘接材料为铝合金AA6061和板材形式的木材，胶粘剂为环氧树脂。分别用砂纸和砂纸对铝和木材粘附样品进行机械磨损获得不同的表面粗糙度。单带接头在室温下进行测试。结果表明，木材和铝粘接接头的粘结强度与表面粗糙度之间存在明显的相关性。最佳表面粗糙度值在Ra = 1.68±0.14°范围内。μm, Ra = 1.64±0.2?μm为铝和木材粘接接头。在粘接接头设计阶段，应考虑表面粗糙度和粘接材料参数。
Effect of surface roughness using different adherend materials on the adhesive bond strength
In this paper, an experimental study on the effect of surface roughness of different adherend material on adhesive bond strength was carried out. The adherend material used was aluminium AA6061 and wood in the form of sheet, and the adhesive was an epoxy resin. Different surface roughness obtained by mechanical abrasion using an emery paper and sand paper for aluminium and wood adherend samples respectively. Single strap joints were tested at room temperature. Results showed that there is clear dependency observed in between the adhesive bond strength and surface roughness of both wood and aluminium adherend joints. Optimum surface roughness values were obtained in the range of Ra?=?1.68?±?0.14?μm and Ra?=?1.64?±?0.2?μm for the aluminium and wood adherend joints respectively. Surface roughness along with the adhered material parameters should be considered during design stage of adhesively bonded joints.
期刊介绍：
Applied Adhesion Science focuses on practical applications of adhesives, with special emphasis in fields such as oil industry, aerospace and biomedicine. Topics related to the phenomena of adhesion and the application of adhesive materials are welcome, especially in biomedical areas such as adhesive dentistry. Both theoretical and experimental works are considered for publication. Applied Adhesion Science is a peer-reviewed open access journal published under the SpringerOpen brand. The journal''s open access policy offers a fast publication workflow whilst maintaining rigorous peer review process.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号