AgNP/TEMPO氧化纤维素纳米纤维/壳聚糖复合纤维的抗菌性能

IF 4 Q2 MATERIALS SCIENCE, MULTIDISCIPLINARY

Fibers Pub Date : 2023-08-14 DOI:10.3390/fib11080069

Duangkamol Dechojarassri, Kazuki Komatsu, A. Sawara, H. Tamura, T. Furuike

{"title":"AgNP/TEMPO氧化纤维素纳米纤维/壳聚糖复合纤维的抗菌性能","authors":"Duangkamol Dechojarassri, Kazuki Komatsu, A. Sawara, H. Tamura, T. Furuike","doi":"10.3390/fib11080069","DOIUrl":null,"url":null,"abstract":"This study successfully synthesized functionalized silver nanoparticle/TEMPO-oxidized cellulose nanofiber/chitosan (AgNP/TOCN/CS) composite fibers. First, the TOCN/CS composite fibers were prepared through the wet-spinning technique, yielding Ag/TOCN/CS composite fibers after immersion in a 5 mM AgNO3 aqueous solution for 3 h, followed by washing with 100 mL of deionized water five times. Second, upon heat treatment without adding other reducing agents, TOCN reduced the Ag+ in the Ag/TOCN/CS composite fibers to AgNP/TOCN/CS composite fibers on the surface of the CS fibers. The fiber color changed from white to yellow-orange when the temperature changed from 100 to 170 °C. In addition, the results suggest that the heat treatment at 130 °C for 20 min was the optimal heat treatment condition. Meanwhile, soaking the fibers in 50 mM ascorbic acid for 1 min is the best condition for ascorbic acid reduction. The antibacterial test results showed that the AgNP/TOCN/CS composite fibers formed via ascorbic acid reduction exhibited better antibacterial activity against both Escherichia coli and Bacillus subtilis than those produced via heat treatment. In summary, AgNPs formed on the fiber surface of AgNP/TOCN/CS composite fibers and showed antibacterial activity, confirming the successful addition of antibacterial properties to TOCN/CS composite fibers.","PeriodicalId":12122,"journal":{"name":"Fibers","volume":" ","pages":""},"PeriodicalIF":4.0000,"publicationDate":"2023-08-14","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Antimicrobial Properties of AgNP/TEMPO-Oxidized Cellulose Nanofiber/Chitosan Composite Fibers\",\"authors\":\"Duangkamol Dechojarassri, Kazuki Komatsu, A. Sawara, H. Tamura, T. Furuike\",\"doi\":\"10.3390/fib11080069\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"This study successfully synthesized functionalized silver nanoparticle/TEMPO-oxidized cellulose nanofiber/chitosan (AgNP/TOCN/CS) composite fibers. First, the TOCN/CS composite fibers were prepared through the wet-spinning technique, yielding Ag/TOCN/CS composite fibers after immersion in a 5 mM AgNO3 aqueous solution for 3 h, followed by washing with 100 mL of deionized water five times. Second, upon heat treatment without adding other reducing agents, TOCN reduced the Ag+ in the Ag/TOCN/CS composite fibers to AgNP/TOCN/CS composite fibers on the surface of the CS fibers. The fiber color changed from white to yellow-orange when the temperature changed from 100 to 170 °C. In addition, the results suggest that the heat treatment at 130 °C for 20 min was the optimal heat treatment condition. Meanwhile, soaking the fibers in 50 mM ascorbic acid for 1 min is the best condition for ascorbic acid reduction. The antibacterial test results showed that the AgNP/TOCN/CS composite fibers formed via ascorbic acid reduction exhibited better antibacterial activity against both Escherichia coli and Bacillus subtilis than those produced via heat treatment. In summary, AgNPs formed on the fiber surface of AgNP/TOCN/CS composite fibers and showed antibacterial activity, confirming the successful addition of antibacterial properties to TOCN/CS composite fibers.\",\"PeriodicalId\":12122,\"journal\":{\"name\":\"Fibers\",\"volume\":\" \",\"pages\":\"\"},\"PeriodicalIF\":4.0000,\"publicationDate\":\"2023-08-14\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Fibers\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.3390/fib11080069\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Fibers","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.3390/fib11080069","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}

引用次数: 0

摘要

本研究成功合成了功能化银纳米粒子/TEMPO氧化纤维素纳米纤维/壳聚糖（AgNP/TOCN/CS）复合纤维。首先，通过湿法纺丝技术制备TOCN/CS复合纤维，在5mM AgNO3水溶液中浸泡3小时后，用100mL去离子水洗涤5次，得到Ag/TOCN/CS复合纤维。其次，在不添加其他还原剂的情况下进行热处理时，TOCN将Ag/TOCN/CS复合纤维中的Ag+还原为CS纤维表面的AgNP/TOCN/CS复合纤维。当温度从100°C变化到170°C时，纤维的颜色从白色变为黄橙色。此外，结果表明，在130°C下热处理20min是最佳的热处理条件。同时，将纤维在50mM抗坏血酸中浸泡1分钟是抗坏血酸还原的最佳条件。抗菌试验结果表明，通过抗坏血酸还原形成的AgNP/TOCN/CS复合纤维对大肠杆菌和枯草芽孢杆菌均表现出比通过热处理产生的纤维更好的抗菌活性。总之，AgNPs在AgNP/TOCN/CS复合纤维的纤维表面形成，并显示出抗菌活性，证实了TOCN/CS复合纤维成功地增加了抗菌性能。

本文章由计算机程序翻译，如有差异，请以英文原文为准。

查看原文本刊更多论文

Antimicrobial Properties of AgNP/TEMPO-Oxidized Cellulose Nanofiber/Chitosan Composite Fibers

This study successfully synthesized functionalized silver nanoparticle/TEMPO-oxidized cellulose nanofiber/chitosan (AgNP/TOCN/CS) composite fibers. First, the TOCN/CS composite fibers were prepared through the wet-spinning technique, yielding Ag/TOCN/CS composite fibers after immersion in a 5 mM AgNO3 aqueous solution for 3 h, followed by washing with 100 mL of deionized water five times. Second, upon heat treatment without adding other reducing agents, TOCN reduced the Ag+ in the Ag/TOCN/CS composite fibers to AgNP/TOCN/CS composite fibers on the surface of the CS fibers. The fiber color changed from white to yellow-orange when the temperature changed from 100 to 170 °C. In addition, the results suggest that the heat treatment at 130 °C for 20 min was the optimal heat treatment condition. Meanwhile, soaking the fibers in 50 mM ascorbic acid for 1 min is the best condition for ascorbic acid reduction. The antibacterial test results showed that the AgNP/TOCN/CS composite fibers formed via ascorbic acid reduction exhibited better antibacterial activity against both Escherichia coli and Bacillus subtilis than those produced via heat treatment. In summary, AgNPs formed on the fiber surface of AgNP/TOCN/CS composite fibers and showed antibacterial activity, confirming the successful addition of antibacterial properties to TOCN/CS composite fibers.

求助全文

通过发布文献求助，成功后即可免费获取论文全文。去求助

来源期刊

Fibers Engineering-Civil and Structural Engineering

CiteScore

7.00

自引率

7.70%

发文量

审稿时长

11 weeks

期刊介绍： Fibers (ISSN 2079-6439) is a peer-reviewed scientific journal that publishes original articles, critical reviews, research notes and short communications on the materials science and all other empirical and theoretical studies of fibers, providing a forum for integrating fiber research across many disciplines. Our aim is to encourage scientists to publish their experimental and theoretical results in as much detail as possible. There is no restriction on the length of the papers. The full experimental details must be provided so that the results can be reproduced. Electronic files or software regarding the full details of the calculation and experimental procedure, if unable to be published in a normal way, can be deposited as supplementary material. The following topics are relevant and within the scope of this journal: -textile fibers -natural fibers and biological microfibrils -metallic fibers -optic fibers -carbon fibers -silicon carbide fibers -fiberglass -mineral fibers -cellulose fibers -polymer fibers -microfibers, nanofibers and nanotubes -new processing methods for fibers -chemistry of fiber materials -physical properties of fibers -exposure to and toxicology of fibers -biokinetics of fibers -the diversity of fiber origins