{"title":"未改性和蒙脱石改性环氧化合物的力学性能。第一部分:压缩试验","authors":"Anna Rudawska","doi":"10.1186/s40563-021-00136-9","DOIUrl":null,"url":null,"abstract":"<div><p>The aim of the article was to determine the compressive strength and compressive strain of an unmodified and a modified epoxy compounds containing a montmorillonite filler, as well as to determine the effect of temperature and an aging time on the mechanical parameters of the considered epoxy compounds. The subject of the research was both the unmodified and the modified adhesive compounds. The unmodified epoxy compounds were made in four variants, which included the epoxy resins based on a bisphenol A as well as the curing agents: a triethylenetetramine and a polyamide curing agent. The modified compounds containing the montmorillonite filler, were also made in four variants. The samples were subjected in a thermal chamber at 80 °C for 1 and 2 months and in a thermal shock chamber in the temperature range from − 40 °C to 80 °C for 1 and 2 months. The reference samples were seasoned at room temperature 20–25 °C. The epoxy compounds samples were subjected to the compression strength tests in accordance with ISO 604 standard. The compressive strength is influenced by the environment and temperature, the aging time and the presence of the modifying agent. The epoxy compounds subjected at elevated or variable temperatures have higher compressive strength than the reference epoxy compounds. The operation of the climatic chamber or the thermal shock chamber makes the samples more deformable than the reference samples.</p></div>","PeriodicalId":464,"journal":{"name":"Applied Adhesion Science","volume":"9 1","pages":""},"PeriodicalIF":1.6800,"publicationDate":"2021-09-26","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://appliedadhesionscience.springeropen.com/counter/pdf/10.1186/s40563-021-00136-9","citationCount":"0","resultStr":"{\"title\":\"Mechanical properties of unmodified and montmorillonite-modified epoxy compounds. Part I: compression test\",\"authors\":\"Anna Rudawska\",\"doi\":\"10.1186/s40563-021-00136-9\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><p>The aim of the article was to determine the compressive strength and compressive strain of an unmodified and a modified epoxy compounds containing a montmorillonite filler, as well as to determine the effect of temperature and an aging time on the mechanical parameters of the considered epoxy compounds. The subject of the research was both the unmodified and the modified adhesive compounds. The unmodified epoxy compounds were made in four variants, which included the epoxy resins based on a bisphenol A as well as the curing agents: a triethylenetetramine and a polyamide curing agent. The modified compounds containing the montmorillonite filler, were also made in four variants. The samples were subjected in a thermal chamber at 80 °C for 1 and 2 months and in a thermal shock chamber in the temperature range from − 40 °C to 80 °C for 1 and 2 months. The reference samples were seasoned at room temperature 20–25 °C. The epoxy compounds samples were subjected to the compression strength tests in accordance with ISO 604 standard. The compressive strength is influenced by the environment and temperature, the aging time and the presence of the modifying agent. The epoxy compounds subjected at elevated or variable temperatures have higher compressive strength than the reference epoxy compounds. The operation of the climatic chamber or the thermal shock chamber makes the samples more deformable than the reference samples.</p></div>\",\"PeriodicalId\":464,\"journal\":{\"name\":\"Applied Adhesion Science\",\"volume\":\"9 1\",\"pages\":\"\"},\"PeriodicalIF\":1.6800,\"publicationDate\":\"2021-09-26\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://appliedadhesionscience.springeropen.com/counter/pdf/10.1186/s40563-021-00136-9\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Applied Adhesion Science\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://link.springer.com/article/10.1186/s40563-021-00136-9\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"Dentistry\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Applied Adhesion Science","FirstCategoryId":"1085","ListUrlMain":"https://link.springer.com/article/10.1186/s40563-021-00136-9","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"Dentistry","Score":null,"Total":0}
引用次数: 0

摘要

文章旨在确定含有蒙脱石填料的未改性和改性环氧化合物的抗压强度和抗压应变,以及温度和老化时间对所考虑的环氧化合物机械参数的影响。研究对象包括未改性和改性粘合剂化合物。未改性环氧化合物有四种变体,包括基于双酚 A 的环氧树脂以及固化剂:三乙烯四胺和聚酰胺固化剂。含有蒙脱石填料的改性化合物也分为四种。样品在温度为 80 °C 的热室中放置 1 个月和 2 个月,在温度为 -40 °C 至 80 °C 的热震室中放置 1 个月和 2 个月。参考样品在室温 20-25 °C下进行了调制。环氧化合物样品按照 ISO 604 标准进行压缩强度测试。抗压强度受环境和温度、老化时间以及改性剂的影响。与参考环氧化合物相比,在高温或变温条件下的环氧化合物具有更高的抗压强度。气候室或热冲击室的操作会使样品比参考样品更容易变形。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
Mechanical properties of unmodified and montmorillonite-modified epoxy compounds. Part I: compression test

The aim of the article was to determine the compressive strength and compressive strain of an unmodified and a modified epoxy compounds containing a montmorillonite filler, as well as to determine the effect of temperature and an aging time on the mechanical parameters of the considered epoxy compounds. The subject of the research was both the unmodified and the modified adhesive compounds. The unmodified epoxy compounds were made in four variants, which included the epoxy resins based on a bisphenol A as well as the curing agents: a triethylenetetramine and a polyamide curing agent. The modified compounds containing the montmorillonite filler, were also made in four variants. The samples were subjected in a thermal chamber at 80 °C for 1 and 2 months and in a thermal shock chamber in the temperature range from − 40 °C to 80 °C for 1 and 2 months. The reference samples were seasoned at room temperature 20–25 °C. The epoxy compounds samples were subjected to the compression strength tests in accordance with ISO 604 standard. The compressive strength is influenced by the environment and temperature, the aging time and the presence of the modifying agent. The epoxy compounds subjected at elevated or variable temperatures have higher compressive strength than the reference epoxy compounds. The operation of the climatic chamber or the thermal shock chamber makes the samples more deformable than the reference samples.

求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
Applied Adhesion Science
Applied Adhesion Science Dentistry-Dentistry (miscellaneous)
自引率
0.00%
发文量
0
审稿时长
13 weeks
期刊介绍: Applied Adhesion Science focuses on practical applications of adhesives, with special emphasis in fields such as oil industry, aerospace and biomedicine. Topics related to the phenomena of adhesion and the application of adhesive materials are welcome, especially in biomedical areas such as adhesive dentistry. Both theoretical and experimental works are considered for publication. Applied Adhesion Science is a peer-reviewed open access journal published under the SpringerOpen brand. The journal''s open access policy offers a fast publication workflow whilst maintaining rigorous peer review process.
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信