Influence of Natural Dentin Biomodification Agent on Push-Out Bond Strength and Nanoleakage of Self-Adhesive Resin Cement Luting of Glass-Fiber Posts.

Objective: To evaluate the plant-derived compound lignin (LIG) as a pretreatment of intraradicular dentin in combination with EDTA on push-out bond strength (PBS) and nanoleakage of the glass fiber posts (GFPs) cemented using adhesive resin cement.

Material and methods: Twenty-eight human incisor roots were prepared for GFP cementation and divided based on dentin pretreatment: (1) CONTROL: no pretreatment, (2) EDTA: 17% EDTA for 3 min, (3) EDTA-LIG: 17% EDTA and 2% lignin for 3 min, (4) EDTA-PAC: 17% EDTA and 2% lignin for 3 min. The GFPs were cemented using the self-adhesive resin cement Multilink Speed. The roots (n = 7) were sectioned into 1 mm-thick discs and subjected to PBS testing after 1 week or 6 months. Nanoleakage was analyzed by SEM. Statistical analysis was performed using two-factor ANOVA and Tukey's test (p < 0.05).

Results: Higher PBS was identified for the CONTROL group (p < 0.001). After 6 months, the EDTA-LIG maintained the bond strength with a predominance of mixed failures, while the EDTA-PAC, EDTA, and CONTROL groups showed reduction of bond strength, with a predominance of adhesive failures along with severe silver infiltration in the interface.

Conclusion: LIG associated with EDTA as a pretreatment for intraradicular dentin shows significant potential for attaining stable bond strength and interfacial integrity of self-adhesive resin cement to intraradicular dentin.