Study on the surface performance strengthening of AlCrN coated cemented carbide by micro-texture laser preparation process

The combined application of coating and surface texture technology on the material surface can enhance its performance. However, the two procedure and their joint mechanism have not been fully revealed. Therefore, this paper takes the micro-textured coated cemented carbide as the research object, and focuses on the influence of preparation procedure and process parameters on surface characteristics and friction behavior. The results show that compared with the coating textured (XT) sample, the textured coating (XW) sample has more advantages in micro-hardness, microstructure and wear degree. The Rockwell hardness of the XT sample is better. Compared with the single coating sample, the coating micro-hardness of the XW sample is increased by 10 %, the Rockwell hardness is reduced by 2 %, the average grain size is reduced by 7.9 %, and the friction force is reduced by 6.2 %. Additionally, within a certain range, the increase of Al content will increase the sample hardness, reduce friction, and inhibit the Cr content and the growth of CrN phase grains. Complete process parameter optimization based on the ideal solution.