Investigation on the Solidification Structure of Q355 in 475 mm Extra-Thick Slabs Adopting Cellular Automaton-Finite Element Model

The solidification structure characteristics are decisive for the production of extra-thick slabs. This study developed a solidification heat transfer model and a cellular automaton–finite element coupled model to investigate the solidification behavior and structure characteristics of a 475 mm extra-thick slab. The models were applied under various continuous casting process parameters and different alloy element content. The simulation results reveal that casting speed has the most significant effect on the solidification behavior of extra-thick slabs, surpassing the impact of specific water flow and superheat. The solidification structure characteristics of the 475 mm extra-thick slabs were investigated under various conditions. The findings indicate that at higher casting speeds and superheats, the average grain size increases and the grain number decreases. The average grain size initially decreases and then increases with the rise in specific water flow, reaching its minimum at approximately 0.17 L·kg−1. Additionally, the average grain radius first decreases and then slightly increases with an increase in carbon content, achieving the minimum value of about 0.17% carbon. Compared with carbon and manganese, silicon has a greater impact on the solidification structure of ultra-thick slabs, and a moderate increase in silicon content can effectively refine the grain size. This study provides a theoretical foundation for understanding the changes in solidification structure characteristics and optimizing continuous casting process parameters for 475 mm extra-thick slabs.