Bing Wang, Hong-lin Zhang, Bin Xu, Ming-yue Sun, Dianzhong Li
{"title":"增材锻造大管锻件的微观结构和机械性能研究","authors":"Bing Wang, Hong-lin Zhang, Bin Xu, Ming-yue Sun, Dianzhong Li","doi":"10.1088/2053-1591/ad6402","DOIUrl":null,"url":null,"abstract":"\n Large-tube forgings were formed using nine layers of continuous-casting billet made from 15CrNi3MoV alloy steel via additive forging. The interfacial microstructural evolution under different hot-compression bonding temperatures and strains was investigated using optical microscopy, scanning electron microscopy, and electron backscatter diffraction. The tensile properties of the hot-compression-bonded and tube-forged samples were also evaluated. The results showed that as the hot-compression bonding temperature and strain increased, the bonding interface gradually disappeared and the voids at the bonding interface closed. Finally, the interface was replaced with recrystallised grains. The tensile properties of the hot-compression-bonded samples at different temperatures and strains were identical. The tensile properties of the interface and base samples of the tube forging were comparable, and the fracture morphologies were consistent. The fracture position of the large tensile sample with a length of 1000 mm containing three original interfaces is the base, indicating the complete metallurgical bonding of the forging","PeriodicalId":18530,"journal":{"name":"Materials Research Express","volume":null,"pages":null},"PeriodicalIF":1.8000,"publicationDate":"2024-07-16","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Investigation on the microstructure and mechanical properties of large-tube forging manufactured by additive forging\",\"authors\":\"Bing Wang, Hong-lin Zhang, Bin Xu, Ming-yue Sun, Dianzhong Li\",\"doi\":\"10.1088/2053-1591/ad6402\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"\\n Large-tube forgings were formed using nine layers of continuous-casting billet made from 15CrNi3MoV alloy steel via additive forging. The interfacial microstructural evolution under different hot-compression bonding temperatures and strains was investigated using optical microscopy, scanning electron microscopy, and electron backscatter diffraction. The tensile properties of the hot-compression-bonded and tube-forged samples were also evaluated. The results showed that as the hot-compression bonding temperature and strain increased, the bonding interface gradually disappeared and the voids at the bonding interface closed. Finally, the interface was replaced with recrystallised grains. The tensile properties of the hot-compression-bonded samples at different temperatures and strains were identical. The tensile properties of the interface and base samples of the tube forging were comparable, and the fracture morphologies were consistent. The fracture position of the large tensile sample with a length of 1000 mm containing three original interfaces is the base, indicating the complete metallurgical bonding of the forging\",\"PeriodicalId\":18530,\"journal\":{\"name\":\"Materials Research Express\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":1.8000,\"publicationDate\":\"2024-07-16\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Materials Research Express\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1088/2053-1591/ad6402\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q3\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Research Express","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1088/2053-1591/ad6402","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
Investigation on the microstructure and mechanical properties of large-tube forging manufactured by additive forging
Large-tube forgings were formed using nine layers of continuous-casting billet made from 15CrNi3MoV alloy steel via additive forging. The interfacial microstructural evolution under different hot-compression bonding temperatures and strains was investigated using optical microscopy, scanning electron microscopy, and electron backscatter diffraction. The tensile properties of the hot-compression-bonded and tube-forged samples were also evaluated. The results showed that as the hot-compression bonding temperature and strain increased, the bonding interface gradually disappeared and the voids at the bonding interface closed. Finally, the interface was replaced with recrystallised grains. The tensile properties of the hot-compression-bonded samples at different temperatures and strains were identical. The tensile properties of the interface and base samples of the tube forging were comparable, and the fracture morphologies were consistent. The fracture position of the large tensile sample with a length of 1000 mm containing three original interfaces is the base, indicating the complete metallurgical bonding of the forging
期刊介绍:
A broad, rapid peer-review journal publishing new experimental and theoretical research on the design, fabrication, properties and applications of all classes of materials.