Critical evaluations on the crystallographic properties of translucent dental zirconia ceramics stabilized with 3-6 mol% yttria

Objectives

This study aimed to determine the crystalline phase composition of 3–6 mol% yttria-stabilized zirconia (3–6YSZ), specifically investigating the presence of tetragonal (t), cubic (c), and/or additional yttria-rich tetragonal (t’) phase.

Methods

Laboratory-fabricated specimens comprising 3–5YSZ, resembling translucent dental zirconia ceramics (TZ specimens), and a blend of 3YSZ and 8YSZ, representing a c-phase reference, were prepared. Additionally, 25 dental zirconia products stabilized with 3–6 mol% yttria were analyzed. Whole X-ray diffraction (XRD) patterns were obtained for Rietveld analysis, complemented by fine scanning in the 2θ region from 72º to 76º for qualitative phase analysis. Moreover, yttria concentrations in each specimen were determined using X-ray fluorescence (XRF) spectroscopy.

Results

In the 2θ region from 72º to 76º, TZ and dental zirconia product specimens displayed four peaks attributed to t- and t’-phases, but the c-phase peak was absent. Rietveld analysis of the whole XRD patterns, utilizing a t-t’ model, demonstrated the t-phase fraction ranging from 86 mass% in 3YSZ to 11 mass% in 6YSZ. Rietveld analysis appeared reliable, as the yttria contents calculated based on lattice parameters aligned well with those measured by XRF. This study established that dental 3–6YSZ consisted of yttria-lean t- and yttria-rich t’-phases.

Significance

The present study enhances understanding of the crystalline structure of dental zirconia ceramics. Future crystallographic analyses of these ceramics should consider the presence of t- and t’-phases.