{"title":"添加锡对 Ti-Al-Sn 合金机械、磨损和电化学性能的影响","authors":"Zafer Gölbaşı , Bülent Öztürk , Kürşat İçin , Sefa Emre Sünbül","doi":"10.1016/j.powtec.2024.119966","DOIUrl":null,"url":null,"abstract":"<div><p>This study aims to investigate the effect of Sn content on the structural, mechanical, wear, and electrochemical properties of Ti-6Al-xSn (x = 3.5–17.5, wt%) alloys fabricated by powder metallurgy method. The results showed that the microhardness generally decreased with increasing Sn content, although there was an unusual increase in microhardness in the alloy with 10.5 wt% Sn. Depending on the Sn content, various phases such as α-Ti, Ti<sub>3</sub>Sn, and Ti<sub>3</sub>Al indicated complex phase formations. The flexural and tensile strengths increased up to 10.5 wt% Sn content, but the strengths reduced above this level. The maximum values for flexural and tensile strengths were obtained as 270 MPa and 125.8 MPa, respectively. With increasing Sn content, the fracture surfaces shifted from cleavage mode to mixed brittle and ductile failure modes. The wear tests were conducted in two different environments: dry and wet conditions. Considering dry sliding conditions, the lowest specific wear rate was obtained as 0.85 × 10<sup>−6</sup> mm<sup>3</sup>/N·m in the alloy coded 3.5Sn at a sliding distance of 1500 m. On the other hand, the highest wear was measured as 2.89 × 10<sup>−6</sup> mm<sup>3</sup>/N·m in the 17.5Sn coded sample at a sliding distance of 6000 m in wet conditions. The wear results demonstrated a relationship between mechanical properties and wear resistance, which was influenced by the existence of porosity. The Ti-6Al-7Sn alloy exhibited the best corrosion resistance with a 2.22 × 10<sup>−7</sup> i<sub>corr</sub> value, while the one with Ti-6Al-17.5Sn alloy showed the worst performance with a 9.71 × 10<sup>−6</sup> i<sub>corr</sub> value.</p></div>","PeriodicalId":407,"journal":{"name":"Powder Technology","volume":null,"pages":null},"PeriodicalIF":4.5000,"publicationDate":"2024-06-03","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Effect of Sn addition on mechanical, wear, and electrochemical properties of Ti-Al-Sn alloys\",\"authors\":\"Zafer Gölbaşı , Bülent Öztürk , Kürşat İçin , Sefa Emre Sünbül\",\"doi\":\"10.1016/j.powtec.2024.119966\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><p>This study aims to investigate the effect of Sn content on the structural, mechanical, wear, and electrochemical properties of Ti-6Al-xSn (x = 3.5–17.5, wt%) alloys fabricated by powder metallurgy method. The results showed that the microhardness generally decreased with increasing Sn content, although there was an unusual increase in microhardness in the alloy with 10.5 wt% Sn. Depending on the Sn content, various phases such as α-Ti, Ti<sub>3</sub>Sn, and Ti<sub>3</sub>Al indicated complex phase formations. The flexural and tensile strengths increased up to 10.5 wt% Sn content, but the strengths reduced above this level. The maximum values for flexural and tensile strengths were obtained as 270 MPa and 125.8 MPa, respectively. With increasing Sn content, the fracture surfaces shifted from cleavage mode to mixed brittle and ductile failure modes. The wear tests were conducted in two different environments: dry and wet conditions. Considering dry sliding conditions, the lowest specific wear rate was obtained as 0.85 × 10<sup>−6</sup> mm<sup>3</sup>/N·m in the alloy coded 3.5Sn at a sliding distance of 1500 m. On the other hand, the highest wear was measured as 2.89 × 10<sup>−6</sup> mm<sup>3</sup>/N·m in the 17.5Sn coded sample at a sliding distance of 6000 m in wet conditions. The wear results demonstrated a relationship between mechanical properties and wear resistance, which was influenced by the existence of porosity. The Ti-6Al-7Sn alloy exhibited the best corrosion resistance with a 2.22 × 10<sup>−7</sup> i<sub>corr</sub> value, while the one with Ti-6Al-17.5Sn alloy showed the worst performance with a 9.71 × 10<sup>−6</sup> i<sub>corr</sub> value.</p></div>\",\"PeriodicalId\":407,\"journal\":{\"name\":\"Powder Technology\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":4.5000,\"publicationDate\":\"2024-06-03\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Powder Technology\",\"FirstCategoryId\":\"5\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S0032591024006090\",\"RegionNum\":2,\"RegionCategory\":\"工程技术\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"ENGINEERING, CHEMICAL\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Powder Technology","FirstCategoryId":"5","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0032591024006090","RegionNum":2,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"ENGINEERING, CHEMICAL","Score":null,"Total":0}
Effect of Sn addition on mechanical, wear, and electrochemical properties of Ti-Al-Sn alloys
This study aims to investigate the effect of Sn content on the structural, mechanical, wear, and electrochemical properties of Ti-6Al-xSn (x = 3.5–17.5, wt%) alloys fabricated by powder metallurgy method. The results showed that the microhardness generally decreased with increasing Sn content, although there was an unusual increase in microhardness in the alloy with 10.5 wt% Sn. Depending on the Sn content, various phases such as α-Ti, Ti3Sn, and Ti3Al indicated complex phase formations. The flexural and tensile strengths increased up to 10.5 wt% Sn content, but the strengths reduced above this level. The maximum values for flexural and tensile strengths were obtained as 270 MPa and 125.8 MPa, respectively. With increasing Sn content, the fracture surfaces shifted from cleavage mode to mixed brittle and ductile failure modes. The wear tests were conducted in two different environments: dry and wet conditions. Considering dry sliding conditions, the lowest specific wear rate was obtained as 0.85 × 10−6 mm3/N·m in the alloy coded 3.5Sn at a sliding distance of 1500 m. On the other hand, the highest wear was measured as 2.89 × 10−6 mm3/N·m in the 17.5Sn coded sample at a sliding distance of 6000 m in wet conditions. The wear results demonstrated a relationship between mechanical properties and wear resistance, which was influenced by the existence of porosity. The Ti-6Al-7Sn alloy exhibited the best corrosion resistance with a 2.22 × 10−7 icorr value, while the one with Ti-6Al-17.5Sn alloy showed the worst performance with a 9.71 × 10−6 icorr value.
期刊介绍:
Powder Technology is an International Journal on the Science and Technology of Wet and Dry Particulate Systems. Powder Technology publishes papers on all aspects of the formation of particles and their characterisation and on the study of systems containing particulate solids. No limitation is imposed on the size of the particles, which may range from nanometre scale, as in pigments or aerosols, to that of mined or quarried materials. The following list of topics is not intended to be comprehensive, but rather to indicate typical subjects which fall within the scope of the journal's interests:
Formation and synthesis of particles by precipitation and other methods.
Modification of particles by agglomeration, coating, comminution and attrition.
Characterisation of the size, shape, surface area, pore structure and strength of particles and agglomerates (including the origins and effects of inter particle forces).
Packing, failure, flow and permeability of assemblies of particles.
Particle-particle interactions and suspension rheology.
Handling and processing operations such as slurry flow, fluidization, pneumatic conveying.
Interactions between particles and their environment, including delivery of particulate products to the body.
Applications of particle technology in production of pharmaceuticals, chemicals, foods, pigments, structural, and functional materials and in environmental and energy related matters.
For materials-oriented contributions we are looking for articles revealing the effect of particle/powder characteristics (size, morphology and composition, in that order) on material performance or functionality and, ideally, comparison to any industrial standard.