润滑滚动/滑动摩擦试验对 100Cr6 轴承钢中氢捕集的影响

IF 2.9 3区 工程技术 Q2 ENGINEERING, CHEMICAL
Lisa-Marie Weniger, Birhan Sefer, Leonardo Pelcastre, Pia Åkerfeldt, Jens Hardell
{"title":"润滑滚动/滑动摩擦试验对 100Cr6 轴承钢中氢捕集的影响","authors":"Lisa-Marie Weniger,&nbsp;Birhan Sefer,&nbsp;Leonardo Pelcastre,&nbsp;Pia Åkerfeldt,&nbsp;Jens Hardell","doi":"10.1007/s11249-024-01871-3","DOIUrl":null,"url":null,"abstract":"<div><p>As hydrogen reduces the fatigue life of 100Cr6 bearing steel significantly, extensive research on the interaction of hydrogen with 100Cr6 is necessary. This study investigated the influence of rolling/sliding tribotesting performed on a micro-pitting-rig on the hydrogen absorption and trapping behaviour of 100Cr6 bearing steel. Thermal desorption mass spectrometry was used to compare the hydrogen desorption spectra of 100Cr6 samples after tribological tests and static heated oil-immersion tests to untested reference samples. The approach was chosen to further understand the influence of both microstructural deformation as well as steel-oil contact on the hydrogen absorption and trapping behaviour of 100Cr6. The tribological test showed a stable friction behaviour and mild wear which was dominated by local plastic deformation of surface asperities. Despite the mild wear, a change in de-trapping temperatures was found for tribotested samples compared to oil-immersed and untested reference samples. This finding indicates that even mild tribotesting conditions alter the hydrogen trapping behaviour of 100Cr6 bearing steel.</p></div>","PeriodicalId":806,"journal":{"name":"Tribology Letters","volume":"72 3","pages":""},"PeriodicalIF":2.9000,"publicationDate":"2024-05-28","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://link.springer.com/content/pdf/10.1007/s11249-024-01871-3.pdf","citationCount":"0","resultStr":"{\"title\":\"Influence of Lubricated Rolling/Sliding Tribotesting on Hydrogen Trapping in 100Cr6 Bearing Steel\",\"authors\":\"Lisa-Marie Weniger,&nbsp;Birhan Sefer,&nbsp;Leonardo Pelcastre,&nbsp;Pia Åkerfeldt,&nbsp;Jens Hardell\",\"doi\":\"10.1007/s11249-024-01871-3\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><p>As hydrogen reduces the fatigue life of 100Cr6 bearing steel significantly, extensive research on the interaction of hydrogen with 100Cr6 is necessary. This study investigated the influence of rolling/sliding tribotesting performed on a micro-pitting-rig on the hydrogen absorption and trapping behaviour of 100Cr6 bearing steel. Thermal desorption mass spectrometry was used to compare the hydrogen desorption spectra of 100Cr6 samples after tribological tests and static heated oil-immersion tests to untested reference samples. The approach was chosen to further understand the influence of both microstructural deformation as well as steel-oil contact on the hydrogen absorption and trapping behaviour of 100Cr6. The tribological test showed a stable friction behaviour and mild wear which was dominated by local plastic deformation of surface asperities. Despite the mild wear, a change in de-trapping temperatures was found for tribotested samples compared to oil-immersed and untested reference samples. This finding indicates that even mild tribotesting conditions alter the hydrogen trapping behaviour of 100Cr6 bearing steel.</p></div>\",\"PeriodicalId\":806,\"journal\":{\"name\":\"Tribology Letters\",\"volume\":\"72 3\",\"pages\":\"\"},\"PeriodicalIF\":2.9000,\"publicationDate\":\"2024-05-28\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://link.springer.com/content/pdf/10.1007/s11249-024-01871-3.pdf\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Tribology Letters\",\"FirstCategoryId\":\"5\",\"ListUrlMain\":\"https://link.springer.com/article/10.1007/s11249-024-01871-3\",\"RegionNum\":3,\"RegionCategory\":\"工程技术\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"ENGINEERING, CHEMICAL\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Tribology Letters","FirstCategoryId":"5","ListUrlMain":"https://link.springer.com/article/10.1007/s11249-024-01871-3","RegionNum":3,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"ENGINEERING, CHEMICAL","Score":null,"Total":0}
引用次数: 0

摘要

由于氢会显著降低 100Cr6 轴承钢的疲劳寿命,因此有必要对氢与 100Cr6 的相互作用进行广泛研究。本研究调查了在微点蚀钻机上进行的滚动/滑动磨擦试验对 100Cr6 轴承钢吸氢和捕氢行为的影响。采用热解吸质谱法比较了 100Cr6 试样在摩擦学测试和静态加热油浸泡测试后与未测试参考试样的氢解吸光谱。选择这种方法是为了进一步了解微结构变形以及钢-油接触对 100Cr6 吸氢和捕氢行为的影响。摩擦学测试表明,摩擦行为稳定,磨损轻微,主要是表面尖角的局部塑性变形。尽管磨损轻微,但与浸油和未测试的参考样品相比,经过摩擦测试的样品的脱捕温度发生了变化。这一发现表明,即使是温和的摩擦试验条件也会改变 100Cr6 轴承钢的氢捕集行为。
本文章由计算机程序翻译,如有差异,请以英文原文为准。

Influence of Lubricated Rolling/Sliding Tribotesting on Hydrogen Trapping in 100Cr6 Bearing Steel

Influence of Lubricated Rolling/Sliding Tribotesting on Hydrogen Trapping in 100Cr6 Bearing Steel

As hydrogen reduces the fatigue life of 100Cr6 bearing steel significantly, extensive research on the interaction of hydrogen with 100Cr6 is necessary. This study investigated the influence of rolling/sliding tribotesting performed on a micro-pitting-rig on the hydrogen absorption and trapping behaviour of 100Cr6 bearing steel. Thermal desorption mass spectrometry was used to compare the hydrogen desorption spectra of 100Cr6 samples after tribological tests and static heated oil-immersion tests to untested reference samples. The approach was chosen to further understand the influence of both microstructural deformation as well as steel-oil contact on the hydrogen absorption and trapping behaviour of 100Cr6. The tribological test showed a stable friction behaviour and mild wear which was dominated by local plastic deformation of surface asperities. Despite the mild wear, a change in de-trapping temperatures was found for tribotested samples compared to oil-immersed and untested reference samples. This finding indicates that even mild tribotesting conditions alter the hydrogen trapping behaviour of 100Cr6 bearing steel.

求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
Tribology Letters
Tribology Letters 工程技术-工程:化工
CiteScore
5.30
自引率
9.40%
发文量
116
审稿时长
2.5 months
期刊介绍: Tribology Letters is devoted to the development of the science of tribology and its applications, particularly focusing on publishing high-quality papers at the forefront of tribological science and that address the fundamentals of friction, lubrication, wear, or adhesion. The journal facilitates communication and exchange of seminal ideas among thousands of practitioners who are engaged worldwide in the pursuit of tribology-based science and technology.
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信