Role of Nanotitania Ceramic Particulate Filler on Mechanical and Wear Behaviour of Dental Composite

Nanotitania is a well-acceptable material in biomedical applications due to its excellent biocompatibility. However, its other performances in terms of physical properties, mechanical properties and specific wear rate have been the keen interest of researchers. The study aims to modify dental composite formulation by adding nanotitania filler in different mass fractions and study to investigate its influence on physical and mechanical properties. A conventional monomer matrix consisting of Bisphenol A-Glycidyl methacrylate (BisGMA), Urethane dimethacrylate (UDMA), Triethylene glycol dimethacrylate (TEGDMA), Camphor Quinone (CO), Ethyl-4-dimethylaminobenzoate (EDMAB) was first added and modified with varying nanotitania filler fractions (0,0.5,1,1.5 wt. %). The performance of newly formulated composites was investigated in four major parameters like apparent porosity, hardness, compressive strength and specific wear rate. All tests are performed as per ISO4049 standard which are requirements for fabrication, characterization, direct/indirect restoration of dental composite, inlays, onlays, veneers, crowns and bridges. Specific wear rate was estimated using pin on disk tribometer under constant load of 20N. Due to its extremely hard and brittle nature, the micro-hardness and compressive strength of resin composite on adding 0.5 wt.-% of nanotitania filler fraction (DC0.5TiO2) were increased by 68% and 16% respectively. Using a pin on disc tribometer, a wear assessment has been performed and it was found that under constant wear parameters and distilled water environmental conditions, the specific wear rate was decreased by 26 % on adding 0.5 wt.-% mass fraction of nanotitania. Nanotitania indicated excellent performance based on mechanical and wear properties and hence, it can be suggested to use nanotitania as a novel filler of dental composite for the replacement of other non-biocompatible ceramic filler.