{"title":"氧化锆基台界面的强度是否取决于水泥、氧化锆类型和钛基台尺寸?","authors":"Zumreta Alic , Tom Vaskovich , Alexander Franz , Stefan Lettner , Andreas Moritz , David C. Watts , Andreas Schedle","doi":"10.1016/j.dental.2024.04.003","DOIUrl":null,"url":null,"abstract":"<div><h3>Objectives</h3><p>Part 1 of this study investigates the influence of zirconia types, chimney heights, and gingival heights on the strength of the zirconia-abutment-interface. Part 2 extends the analysis to include adhesive brands and macro-retentions.</p></div><div><h3>Methods</h3><p>In Part 1, the study utilized three zirconia types (700 MPa, 1000 MPa, 1200 MPa) to fabricate 234 screw-retained zirconia crowns with varying chimney heights (3.5 mm, 4.1 mm, 5 mm) and gingival heights (0.65 mm, 1.2 mm, 3 mm) of the titanium abutments. All adherend surfaces underwent sandblasting with aluminum oxide before cementation with a specific resin cement. In Part 2, the investigation of 240 screw-retained zirconia crowns focused on a single zirconia type (1000 MPa) with chimney heights of 3.5 mm and 5 mm and a gingival height of 0.65 mm of the titanium abutments, cemented with three different resin cements. All adherent surfaces underwent sandblasting with aluminum oxide before cementation, whereas 120 out of 240 abutments received additional macro retentions. Storage in water at 37 °C for 24 h preceded the tensile test.</p></div><div><h3>Results</h3><p>The study revealed a substantial impact of chimney height and zirconia type on the bond strength of the zirconia-abutment-interface. Neither adhesive brands nor macro retentions significantly impacted the bond strength. Fracture incidence was significantly influenced by gingival height and zirconia type in part 1, whereas in part 2 smaller chimney heights correlated with a higher fracture incidence.</p></div><div><h3>Significance</h3><p>This study contributes insights into the complex interplay of factors influencing the zirconia-abutment-interface. The results provide a foundation for refining clinical approaches, emphasizing the importance of chimney height and zirconia type in achieving successful anterior gap implant restorations.</p></div>","PeriodicalId":298,"journal":{"name":"Dental Materials","volume":null,"pages":null},"PeriodicalIF":4.6000,"publicationDate":"2024-06-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.sciencedirect.com/science/article/pii/S0109564124000824/pdfft?md5=751aa22e7623c11baf5bf0fa18dade35&pid=1-s2.0-S0109564124000824-main.pdf","citationCount":"0","resultStr":"{\"title\":\"Do strength of zirconia-abutment-interfaces depend on cement, zirconia type and titanium abutment dimensions?\",\"authors\":\"Zumreta Alic , Tom Vaskovich , Alexander Franz , Stefan Lettner , Andreas Moritz , David C. Watts , Andreas Schedle\",\"doi\":\"10.1016/j.dental.2024.04.003\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><h3>Objectives</h3><p>Part 1 of this study investigates the influence of zirconia types, chimney heights, and gingival heights on the strength of the zirconia-abutment-interface. Part 2 extends the analysis to include adhesive brands and macro-retentions.</p></div><div><h3>Methods</h3><p>In Part 1, the study utilized three zirconia types (700 MPa, 1000 MPa, 1200 MPa) to fabricate 234 screw-retained zirconia crowns with varying chimney heights (3.5 mm, 4.1 mm, 5 mm) and gingival heights (0.65 mm, 1.2 mm, 3 mm) of the titanium abutments. All adherend surfaces underwent sandblasting with aluminum oxide before cementation with a specific resin cement. In Part 2, the investigation of 240 screw-retained zirconia crowns focused on a single zirconia type (1000 MPa) with chimney heights of 3.5 mm and 5 mm and a gingival height of 0.65 mm of the titanium abutments, cemented with three different resin cements. All adherent surfaces underwent sandblasting with aluminum oxide before cementation, whereas 120 out of 240 abutments received additional macro retentions. Storage in water at 37 °C for 24 h preceded the tensile test.</p></div><div><h3>Results</h3><p>The study revealed a substantial impact of chimney height and zirconia type on the bond strength of the zirconia-abutment-interface. Neither adhesive brands nor macro retentions significantly impacted the bond strength. Fracture incidence was significantly influenced by gingival height and zirconia type in part 1, whereas in part 2 smaller chimney heights correlated with a higher fracture incidence.</p></div><div><h3>Significance</h3><p>This study contributes insights into the complex interplay of factors influencing the zirconia-abutment-interface. The results provide a foundation for refining clinical approaches, emphasizing the importance of chimney height and zirconia type in achieving successful anterior gap implant restorations.</p></div>\",\"PeriodicalId\":298,\"journal\":{\"name\":\"Dental Materials\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":4.6000,\"publicationDate\":\"2024-06-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://www.sciencedirect.com/science/article/pii/S0109564124000824/pdfft?md5=751aa22e7623c11baf5bf0fa18dade35&pid=1-s2.0-S0109564124000824-main.pdf\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Dental Materials\",\"FirstCategoryId\":\"5\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S0109564124000824\",\"RegionNum\":1,\"RegionCategory\":\"医学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"DENTISTRY, ORAL SURGERY & MEDICINE\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Dental Materials","FirstCategoryId":"5","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0109564124000824","RegionNum":1,"RegionCategory":"医学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"DENTISTRY, ORAL SURGERY & MEDICINE","Score":null,"Total":0}
Do strength of zirconia-abutment-interfaces depend on cement, zirconia type and titanium abutment dimensions?
Objectives
Part 1 of this study investigates the influence of zirconia types, chimney heights, and gingival heights on the strength of the zirconia-abutment-interface. Part 2 extends the analysis to include adhesive brands and macro-retentions.
Methods
In Part 1, the study utilized three zirconia types (700 MPa, 1000 MPa, 1200 MPa) to fabricate 234 screw-retained zirconia crowns with varying chimney heights (3.5 mm, 4.1 mm, 5 mm) and gingival heights (0.65 mm, 1.2 mm, 3 mm) of the titanium abutments. All adherend surfaces underwent sandblasting with aluminum oxide before cementation with a specific resin cement. In Part 2, the investigation of 240 screw-retained zirconia crowns focused on a single zirconia type (1000 MPa) with chimney heights of 3.5 mm and 5 mm and a gingival height of 0.65 mm of the titanium abutments, cemented with three different resin cements. All adherent surfaces underwent sandblasting with aluminum oxide before cementation, whereas 120 out of 240 abutments received additional macro retentions. Storage in water at 37 °C for 24 h preceded the tensile test.
Results
The study revealed a substantial impact of chimney height and zirconia type on the bond strength of the zirconia-abutment-interface. Neither adhesive brands nor macro retentions significantly impacted the bond strength. Fracture incidence was significantly influenced by gingival height and zirconia type in part 1, whereas in part 2 smaller chimney heights correlated with a higher fracture incidence.
Significance
This study contributes insights into the complex interplay of factors influencing the zirconia-abutment-interface. The results provide a foundation for refining clinical approaches, emphasizing the importance of chimney height and zirconia type in achieving successful anterior gap implant restorations.
期刊介绍:
Dental Materials publishes original research, review articles, and short communications.
Academy of Dental Materials members click here to register for free access to Dental Materials online.
The principal aim of Dental Materials is to promote rapid communication of scientific information between academia, industry, and the dental practitioner. Original Manuscripts on clinical and laboratory research of basic and applied character which focus on the properties or performance of dental materials or the reaction of host tissues to materials are given priority publication. Other acceptable topics include application technology in clinical dentistry and dental laboratory technology.
Comprehensive reviews and editorial commentaries on pertinent subjects will be considered.