氢脆对用于 FCEV 氢气阀门的 DLC 涂层机械特性的影响

IF 6.6 2区 材料科学 Q1 MATERIALS SCIENCE, MULTIDISCIPLINARY
Dong-Ho Shin, Seong-Jong Kim
{"title":"氢脆对用于 FCEV 氢气阀门的 DLC 涂层机械特性的影响","authors":"Dong-Ho Shin, Seong-Jong Kim","doi":"10.1038/s41529-024-00460-y","DOIUrl":null,"url":null,"abstract":"Diamond-like carbon (DLC) coating is a surface coating technology with excellent hydrogen permeation resistance and wear resistance. However, it is difficult to completely prevent hydrogen permeation, and when hydrogen penetrates into the coating layer, the DLC coating is adversely affected. Therefore, we investigated the effect of hydrogen embrittlement on the adhesion strength and wear resistance of the DLC coating layer. As the results of the research, the surface roughness of the DLC coating was increased by a maximum of 3.8 times with hydrogen charging, and the delamination ratio of the DLC coating reached about 58%. In addition, the Lc3, which refers to the adhesion strength corresponding to the complete delamination of the DLC coating, was decreased by a maximum of 2.0 N due to hydrogen permeation. In addition, the wear resistance decreased due to hydrogen permeation, and the exposed width of the substrate due to wear increased by more than 4 times. It was also determined that hydrogen blistering or hydrogen-induced cracking occurred at the interface between the DLC coating and the chromium buffer layer due to hydrogen permeation, which decreased the durability of the DLC coating.","PeriodicalId":19270,"journal":{"name":"npj Materials Degradation","volume":null,"pages":null},"PeriodicalIF":6.6000,"publicationDate":"2024-05-04","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.nature.com/articles/s41529-024-00460-y.pdf","citationCount":"0","resultStr":"{\"title\":\"Effect of hydrogen embrittlement on mechanical characteristics of DLC-coating for hydrogen valves of FCEVs\",\"authors\":\"Dong-Ho Shin, Seong-Jong Kim\",\"doi\":\"10.1038/s41529-024-00460-y\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Diamond-like carbon (DLC) coating is a surface coating technology with excellent hydrogen permeation resistance and wear resistance. However, it is difficult to completely prevent hydrogen permeation, and when hydrogen penetrates into the coating layer, the DLC coating is adversely affected. Therefore, we investigated the effect of hydrogen embrittlement on the adhesion strength and wear resistance of the DLC coating layer. As the results of the research, the surface roughness of the DLC coating was increased by a maximum of 3.8 times with hydrogen charging, and the delamination ratio of the DLC coating reached about 58%. In addition, the Lc3, which refers to the adhesion strength corresponding to the complete delamination of the DLC coating, was decreased by a maximum of 2.0 N due to hydrogen permeation. In addition, the wear resistance decreased due to hydrogen permeation, and the exposed width of the substrate due to wear increased by more than 4 times. It was also determined that hydrogen blistering or hydrogen-induced cracking occurred at the interface between the DLC coating and the chromium buffer layer due to hydrogen permeation, which decreased the durability of the DLC coating.\",\"PeriodicalId\":19270,\"journal\":{\"name\":\"npj Materials Degradation\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":6.6000,\"publicationDate\":\"2024-05-04\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://www.nature.com/articles/s41529-024-00460-y.pdf\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"npj Materials Degradation\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://www.nature.com/articles/s41529-024-00460-y\",\"RegionNum\":2,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"npj Materials Degradation","FirstCategoryId":"88","ListUrlMain":"https://www.nature.com/articles/s41529-024-00460-y","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0

摘要

类金刚石碳(DLC)涂层是一种表面涂层技术,具有优异的抗氢渗透性和耐磨性。然而,氢渗透很难完全避免,当氢渗入涂层时,DLC 涂层会受到不利影响。因此,我们研究了氢脆对 DLC 涂层层附着强度和耐磨性的影响。研究结果表明,在充氢的情况下,DLC 涂层的表面粗糙度最大增加了 3.8 倍,DLC 涂层的分层率达到了约 58%。此外,由于氢的渗透,DLC 涂层完全分层时的附着强度 Lc3 最大下降了 2.0 N。此外,氢渗透还导致耐磨性下降,基底因磨损而暴露的宽度增加了 4 倍多。研究还发现,由于氢的渗透,DLC 涂层和铬缓冲层之间的界面出现了氢起泡或氢致裂纹,从而降低了 DLC 涂层的耐久性。
本文章由计算机程序翻译,如有差异,请以英文原文为准。

Effect of hydrogen embrittlement on mechanical characteristics of DLC-coating for hydrogen valves of FCEVs

Effect of hydrogen embrittlement on mechanical characteristics of DLC-coating for hydrogen valves of FCEVs

Effect of hydrogen embrittlement on mechanical characteristics of DLC-coating for hydrogen valves of FCEVs
Diamond-like carbon (DLC) coating is a surface coating technology with excellent hydrogen permeation resistance and wear resistance. However, it is difficult to completely prevent hydrogen permeation, and when hydrogen penetrates into the coating layer, the DLC coating is adversely affected. Therefore, we investigated the effect of hydrogen embrittlement on the adhesion strength and wear resistance of the DLC coating layer. As the results of the research, the surface roughness of the DLC coating was increased by a maximum of 3.8 times with hydrogen charging, and the delamination ratio of the DLC coating reached about 58%. In addition, the Lc3, which refers to the adhesion strength corresponding to the complete delamination of the DLC coating, was decreased by a maximum of 2.0 N due to hydrogen permeation. In addition, the wear resistance decreased due to hydrogen permeation, and the exposed width of the substrate due to wear increased by more than 4 times. It was also determined that hydrogen blistering or hydrogen-induced cracking occurred at the interface between the DLC coating and the chromium buffer layer due to hydrogen permeation, which decreased the durability of the DLC coating.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
npj Materials Degradation
npj Materials Degradation MATERIALS SCIENCE, MULTIDISCIPLINARY-
CiteScore
7.80
自引率
7.80%
发文量
86
审稿时长
6 weeks
期刊介绍: npj Materials Degradation considers basic and applied research that explores all aspects of the degradation of metallic and non-metallic materials. The journal broadly defines ‘materials degradation’ as a reduction in the ability of a material to perform its task in-service as a result of environmental exposure. The journal covers a broad range of topics including but not limited to: -Degradation of metals, glasses, minerals, polymers, ceramics, cements and composites in natural and engineered environments, as a result of various stimuli -Computational and experimental studies of degradation mechanisms and kinetics -Characterization of degradation by traditional and emerging techniques -New approaches and technologies for enhancing resistance to degradation -Inspection and monitoring techniques for materials in-service, such as sensing technologies
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信