Analysis of the Microstructure and Hardness of Flake Graphite Cast Iron Using the Barkhausen Noise Method and Conventional Techniques

The new brake disc was evaluated for microstructure and hardness by the conventional destructive tests and non-destructive Barkhausen noise method (BNM). Ten non-destructive measurements were carried out in different areas of a brake disc, which were then cut out and made into metallographic test samples. Qualitative and quantitative analysis of graphite precipitates was performed to assess their volume in material matrix, anisotropy and size. Subsequently, graphs showing the relationships between selected stereological parameters of graphite precipitates and parameters determined from the RMS envelope of Barkhausen noise were elucidated. Similar relationships between hardness and parameters coming from non-destructive tests were carried out. Magnetic parameters that specified the size of a graphite precipitate was selected. In addition, repeatability studies using BNM were carried out in the areas of the material with the smallest and largest average size of graphite precipitates. A linear relationship between amplitude of BN and length of graphite flakes was found. The paper presents the possibilities of assessing the volume and size of graphite precipitates, as well as cast iron hardness using BNM.