Tribological behaviour of TiAlN and AlCrN coatings on stainless steel

TiAlN and AlCrN coatings are widely used in applications that require high stress resistance. In this work, the tribological behaviour of physical vapour deposition (PVD) TiAlN and AlCrN commercial coatings deposited on AISI martensitic stainless steel is studied. Microstructure of the coatings was analysed by X-ray diffraction (XRD), optical microscopy (OM) and scanning electron microscopy (SEM) and nanohardness was measured. Pin-on-disk and abrasive wear tests were performed. Adhesion was evaluated using Rockwell C Indentation and scratch test. The thickness of both coatings was approximately 3 µm. AlCrN lost 30 and 10 times less volume than TiAlN in pin-on-disk tests, under low and high loads, respectively. The steady friction coefficient value was also lower. This indicated that the AlCrN coating had a better performance under sliding conditions. On the other hand, the mass loss was similar for both coatings under abrasive wear, even under severe conditions. In the scratch tests, TiAlN coating failed at 60 N load and AlCrN coating at 70 N, the latter showing a higher value of critical load. The deformation was similar for both coatings as it could be observed in the profiles obtained by a mechanical profilometer at 60 N, however, AlCrN did not show film delamination. This enhanced performance can be attributed to higher fracture toughness and load carrying capacity, which not only improved the mechanical properties of the coating but also its adhesion to the stainless-steel substrate.