{"title":"铁合金对电弧熔炼法生产的铁钴镍锰钼钒高熵合金性能的影响","authors":"S. H. Güler","doi":"10.55525/tjst.1401275","DOIUrl":null,"url":null,"abstract":"In this study, high entropy FeCoNiMnMoV and FeCoNiMn (Ferro Mo-Ferro-V) alloys were produced by arc melting method.After the arc melting process, the samples were annealed at 1000ᵒC under argon atmosphere for 15 hours.Physical and thermodynamic calculations were performed to determine the properties of the alloy.In the study, both alloys were characterized. For characterization, XRD, SEM, EDS and Micro hardness were taken from the samples.The aim of my study is to examine the effect of using low-priced starting materials on the microstructure of HEA alloy.For this purpose, ferro alloys were added to the alloy.As a result, similar properties were obtained for the microstructure of both alloys.However, it was determined that after heat treatment, the hardness decreased more due to the chemical composition of the ferro alloy.","PeriodicalId":516893,"journal":{"name":"Turkish Journal of Science and Technology","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2024-02-26","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Effect of Ferro-Alloys on the Properties of High Entropy Alloy with FeCoNiMnMoV Composition Produced by Arc-Melting Method\",\"authors\":\"S. H. Güler\",\"doi\":\"10.55525/tjst.1401275\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"In this study, high entropy FeCoNiMnMoV and FeCoNiMn (Ferro Mo-Ferro-V) alloys were produced by arc melting method.After the arc melting process, the samples were annealed at 1000ᵒC under argon atmosphere for 15 hours.Physical and thermodynamic calculations were performed to determine the properties of the alloy.In the study, both alloys were characterized. For characterization, XRD, SEM, EDS and Micro hardness were taken from the samples.The aim of my study is to examine the effect of using low-priced starting materials on the microstructure of HEA alloy.For this purpose, ferro alloys were added to the alloy.As a result, similar properties were obtained for the microstructure of both alloys.However, it was determined that after heat treatment, the hardness decreased more due to the chemical composition of the ferro alloy.\",\"PeriodicalId\":516893,\"journal\":{\"name\":\"Turkish Journal of Science and Technology\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2024-02-26\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Turkish Journal of Science and Technology\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.55525/tjst.1401275\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Turkish Journal of Science and Technology","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.55525/tjst.1401275","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
摘要
在本研究中，采用电弧熔炼法生产了高熵铁钴镍锰钼钒合金和铁钴镍锰合金（铁钼-铁钒合金），电弧熔炼过程结束后，样品在 1000ᵒC 的氩气环境下退火 15 小时。在表征过程中，对样品进行了 XRD、SEM、EDS 和显微硬度测量。我的研究旨在考察使用低价原材料对 HEA 合金微观结构的影响。
Effect of Ferro-Alloys on the Properties of High Entropy Alloy with FeCoNiMnMoV Composition Produced by Arc-Melting Method
In this study, high entropy FeCoNiMnMoV and FeCoNiMn (Ferro Mo-Ferro-V) alloys were produced by arc melting method.After the arc melting process, the samples were annealed at 1000ᵒC under argon atmosphere for 15 hours.Physical and thermodynamic calculations were performed to determine the properties of the alloy.In the study, both alloys were characterized. For characterization, XRD, SEM, EDS and Micro hardness were taken from the samples.The aim of my study is to examine the effect of using low-priced starting materials on the microstructure of HEA alloy.For this purpose, ferro alloys were added to the alloy.As a result, similar properties were obtained for the microstructure of both alloys.However, it was determined that after heat treatment, the hardness decreased more due to the chemical composition of the ferro alloy.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号