{"title":"热处理对 AZ61 镁合金成型性的影响","authors":"Adel Khalid Alfozan","doi":"10.4028/p-bw1228","DOIUrl":null,"url":null,"abstract":"The current paper focuses on enhancing the manufacturability of AZ61 magnesium alloys by heat treatment. Specimens are subjected to solution heat treatment. First, all samples underwent a 15-hour treatment at 415°C before aging at 50°C, 100oC, and 150°C. The specimens were furnace cooled and quenched after achieving the precise aging temperature. The results have been extracted from tensile and cupping tests. The outcomes of each test have been compared with the data taken without heat treatment, so the ductility increase can be observed. Tests revealed better results for furnace-cooled specimens. The increase in formability of about 9% along with a decrease in strength of only 11% is observed for 150°C aging temperature.","PeriodicalId":21754,"journal":{"name":"Solid State Phenomena","volume":"28 8","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2024-03-18","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Effect of Heat Treatment on Formability of AZ61 Magnesium Alloys\",\"authors\":\"Adel Khalid Alfozan\",\"doi\":\"10.4028/p-bw1228\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The current paper focuses on enhancing the manufacturability of AZ61 magnesium alloys by heat treatment. Specimens are subjected to solution heat treatment. First, all samples underwent a 15-hour treatment at 415°C before aging at 50°C, 100oC, and 150°C. The specimens were furnace cooled and quenched after achieving the precise aging temperature. The results have been extracted from tensile and cupping tests. The outcomes of each test have been compared with the data taken without heat treatment, so the ductility increase can be observed. Tests revealed better results for furnace-cooled specimens. The increase in formability of about 9% along with a decrease in strength of only 11% is observed for 150°C aging temperature.\",\"PeriodicalId\":21754,\"journal\":{\"name\":\"Solid State Phenomena\",\"volume\":\"28 8\",\"pages\":\"\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2024-03-18\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Solid State Phenomena\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.4028/p-bw1228\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Solid State Phenomena","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.4028/p-bw1228","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Effect of Heat Treatment on Formability of AZ61 Magnesium Alloys
The current paper focuses on enhancing the manufacturability of AZ61 magnesium alloys by heat treatment. Specimens are subjected to solution heat treatment. First, all samples underwent a 15-hour treatment at 415°C before aging at 50°C, 100oC, and 150°C. The specimens were furnace cooled and quenched after achieving the precise aging temperature. The results have been extracted from tensile and cupping tests. The outcomes of each test have been compared with the data taken without heat treatment, so the ductility increase can be observed. Tests revealed better results for furnace-cooled specimens. The increase in formability of about 9% along with a decrease in strength of only 11% is observed for 150°C aging temperature.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号