{"title":"TiAlCr-Y涂层Ti45Al8Nb在750°C - 950°C之间的耐高温空气氧化性","authors":"T. Dudziak, P. Datta, H. Du, I. Ross","doi":"10.2478/s13531-013-0132-7","DOIUrl":null,"url":null,"abstract":"This study is concerned with air oxidation of TiAlCr-Y coated Ti45Al-8Nb (at%) alloy between 750 °C–950 °C for 500 hours. It was shown in these tests that at 750 °C, 850 °C and 950 °C, the oxidation degradation increased with temperature: at 750 °C the oxide scale consisted of TiO2/Al2O3/Cr2O3 phases, whilst at 850 °C the oxide scale consisted of TiO2/Al2O3 phases with a small amount of Cr2O3, and larger number of voids. The material exposed at 950 °C showed a significant formation of TiO2 with a small amount of Al2O3 and high number of voids; the formation of Cr2O3 at 950 °C was inhibited mainly due to the formation of volatile CrO3 or CrO2(OH)2 phase.","PeriodicalId":407983,"journal":{"name":"Central European Journal of Engineering","volume":"131 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2013-12-11","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"6","resultStr":"{\"title\":\"High temperature air oxidation resistance of TiAlCr-Y coated Ti45Al8Nb between 750 °C – 950 °C\",\"authors\":\"T. Dudziak, P. Datta, H. Du, I. Ross\",\"doi\":\"10.2478/s13531-013-0132-7\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"This study is concerned with air oxidation of TiAlCr-Y coated Ti45Al-8Nb (at%) alloy between 750 °C–950 °C for 500 hours. It was shown in these tests that at 750 °C, 850 °C and 950 °C, the oxidation degradation increased with temperature: at 750 °C the oxide scale consisted of TiO2/Al2O3/Cr2O3 phases, whilst at 850 °C the oxide scale consisted of TiO2/Al2O3 phases with a small amount of Cr2O3, and larger number of voids. The material exposed at 950 °C showed a significant formation of TiO2 with a small amount of Al2O3 and high number of voids; the formation of Cr2O3 at 950 °C was inhibited mainly due to the formation of volatile CrO3 or CrO2(OH)2 phase.\",\"PeriodicalId\":407983,\"journal\":{\"name\":\"Central European Journal of Engineering\",\"volume\":\"131 1\",\"pages\":\"0\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2013-12-11\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"6\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Central European Journal of Engineering\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.2478/s13531-013-0132-7\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Central European Journal of Engineering","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.2478/s13531-013-0132-7","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
High temperature air oxidation resistance of TiAlCr-Y coated Ti45Al8Nb between 750 °C – 950 °C
This study is concerned with air oxidation of TiAlCr-Y coated Ti45Al-8Nb (at%) alloy between 750 °C–950 °C for 500 hours. It was shown in these tests that at 750 °C, 850 °C and 950 °C, the oxidation degradation increased with temperature: at 750 °C the oxide scale consisted of TiO2/Al2O3/Cr2O3 phases, whilst at 850 °C the oxide scale consisted of TiO2/Al2O3 phases with a small amount of Cr2O3, and larger number of voids. The material exposed at 950 °C showed a significant formation of TiO2 with a small amount of Al2O3 and high number of voids; the formation of Cr2O3 at 950 °C was inhibited mainly due to the formation of volatile CrO3 or CrO2(OH)2 phase.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号