Isıl işlem sonrası poliüretan vernik uygulanmış kestane odununda salınımsal sertlik üzerine yapay yaşlandırmanın etkileri

The effects of artificial weathering (576 h) on the pendulum hardness values of Anatolian chestnut (Castanea sativa Mill.) wood applied with polyurethane varnish (PU) after heat treatment at 190℃ for 1.5 h and at 212℃ for 2 h were investigated. The results revealed that heat treatment, weathering period, and interaction were significant. The hardness values of the heat-treated materials were higher than those of the non-heat-treated test samples. The highest hardness value was determined in the un-weathered group of the test samples that were heat-treated at 190°C for 1.5 h while the lowest value was determined in the group that was heat-treated at 190°C for 1.5 h and weathered for 432 h. The highest reduction rates after weathering were obtained on samples that were heat-treated at 190℃ for 1.5 h, followed by heat-treated at 212℃ for 2 h and non-heat-treated. It was observed that the heat treatment application caused different pendulum hardness values in chestnut wood samples covered with polyurethane varnish.