{"title":"一种用于平面光波电路的高性能光聚合物","authors":"I. McEwan, N. Suyal, X. Li, F. Tooley","doi":"10.1109/FOPC.2002.1015816","DOIUrl":null,"url":null,"abstract":"Development of a novel multifunctional acrylate based photo-polymer formulation with T/sub g/ >150/spl deg/C and its application in the fabrication of optical waveguides is reported. Single mode planar optical waveguides were fabricated using UV exposure through a mask followed by development. Waveguide losses at 1550, 1300 and 850 nm as measured using cutback method were 0.7, 0.4 and 0.05 dB/cm respectively. Birefringence in polymer films was around 1 /spl times/ 10/sup -3/. Waveguides subjected to 85/spl deg/C, under 85% relative humidity conditions showed no deterioration or delamination.","PeriodicalId":117784,"journal":{"name":"Proceedings of 2002 IEEE/LEOS Workshop on Fibre and Optical Passive Components (Cat.No.02EX595)","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2002-08-07","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"5","resultStr":"{\"title\":\"A high performance optical photo-polymer for planar lightwave circuits\",\"authors\":\"I. McEwan, N. Suyal, X. Li, F. Tooley\",\"doi\":\"10.1109/FOPC.2002.1015816\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Development of a novel multifunctional acrylate based photo-polymer formulation with T/sub g/ >150/spl deg/C and its application in the fabrication of optical waveguides is reported. Single mode planar optical waveguides were fabricated using UV exposure through a mask followed by development. Waveguide losses at 1550, 1300 and 850 nm as measured using cutback method were 0.7, 0.4 and 0.05 dB/cm respectively. Birefringence in polymer films was around 1 /spl times/ 10/sup -3/. Waveguides subjected to 85/spl deg/C, under 85% relative humidity conditions showed no deterioration or delamination.\",\"PeriodicalId\":117784,\"journal\":{\"name\":\"Proceedings of 2002 IEEE/LEOS Workshop on Fibre and Optical Passive Components (Cat.No.02EX595)\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2002-08-07\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"5\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Proceedings of 2002 IEEE/LEOS Workshop on Fibre and Optical Passive Components (Cat.No.02EX595)\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1109/FOPC.2002.1015816\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Proceedings of 2002 IEEE/LEOS Workshop on Fibre and Optical Passive Components (Cat.No.02EX595)","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1109/FOPC.2002.1015816","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
A high performance optical photo-polymer for planar lightwave circuits
Development of a novel multifunctional acrylate based photo-polymer formulation with T/sub g/ >150/spl deg/C and its application in the fabrication of optical waveguides is reported. Single mode planar optical waveguides were fabricated using UV exposure through a mask followed by development. Waveguide losses at 1550, 1300 and 850 nm as measured using cutback method were 0.7, 0.4 and 0.05 dB/cm respectively. Birefringence in polymer films was around 1 /spl times/ 10/sup -3/. Waveguides subjected to 85/spl deg/C, under 85% relative humidity conditions showed no deterioration or delamination.