APPROACH TO FERROMAGNETIC SATURATION FOR AMORPHOUS FE-BASED ALLOY

The paper presents the results of research on the structure and selected properties of magnetic alloys based on Fe. The alloy with the chemical composition Fe36Co36Y8B20 was produced using two methods: forcing and sucking the liquid alloy into a copper mould. The alloy was cast in the form of 10 mm × 5 mm × 0.5 mm tiles. The structure of the obtained alloys was examined using X-ray diffraction. The measured diffractograms are typical for amorphous materials. Using the Faraday magnetic balance, the magnetic saturation polarisation curves as a function of temperature were recorded. The Curie temperature of the created alloys, which amounted to approximately 750 K, was determined on the basis of numerical analysis. The original magnetisation curves and static magnetic hysteresis loops were measured using a vibration magnetometer. The produced alloys had a saturation magnetisation of about 1.1T and a coercive field value of about 200 A/m. The curves of primary magnetisation were analysed using H. Kronmüller’s theory. It was found that the magnetising process in the area called the ‘approach to ferromagnetic saturation’ is related to the rotation of the magnetisation vector around the linear defects of the structure.