Radiation grafting of hydrophilic monomers onto poly(4‐methylpentene‐1), II. Grafting of long chain monomers and physical properties of the grafted films

Abstract

Radiation grafting of 2-hydroxyethyl methacrylate (HEMA) and methoxytetraethyleneglycol methacrylate (M4G) on low crystallinity poly(4-methylpentene-1) (TPX) has been investigated. Grafting yield increased with increasing pre-irradiation dose, grafting temperature, and monomer concentration. Grafting rate depends on length of molecular chain in the monomers and decreases with increasing chain length. The grafting yields of electron beam irradiated samples were higher than those of γ-irradiated ones because of higher radical concentration. Tensile strength of the grafted film in the dried state increased and the elongation at break decreased with increasing degree of grafting. On the other hand, in the wet state, the tensile strength and elongation at break decreased with increasing the degree of grafting due to the lack of hydrogen bonds between the grafted chains caused by increased water absorption. Die strahleninduzierte Pfropfung von 2-Hydroxyethylmethacrylat (HEMA) und Methoxytetraethylenglycolmethacrylat (M4G) auf Poly(4-methylpenten-1) (TPX) wurde untersucht. Die Pfropfungsgrade erhohten sich mit zunehmender Vorbestrahlungsdosis, Pfropfungstemperatur und Monomerkonzentration. Die Pfropfungsgeschwindigkeit ist abhangig von der Kettenlange der Monomeren; sie nimmt mit wachsender Kettenlange ab. Bei Bestrahlen der Filme mit Elektronenstrahlen anstelle von γ-Strahlen waren die Pfropfungsgrade hoher. Die Zugfestigkeit der gepfropften Filme im trockenen Zustand stieg mit zunehmendem Pfropfungsgrad an, wahrend die Bruchdehnung abnahm. Dagegen nahmen die Zugfestigkeit und die Bruchdehnung im nassen Zustand mit wachsendem Pfropfungsgrad ab, da Wasserstoffbruckenbindungen zwischen den aufgepfropften Ketten durch die Wasseraufnahme der Filme fehlten.