Prestandardization study on mode I interlaminar fracture toughness test for CFRP in Japan

Abstract

This paper summarizes results from a series of interlaboratory round robin tests (RRTs) performed in order to establish a JIS standard for mode I interlaminar fracture toughness test using double cantilever beam (DCB) specimens. For the case of unidirectional laminates, brittle and toughened CF/epoxy, and CF/PEEK systems were used. Only a brittle CF/epoxy system was used for woven laminates. The round robin tests were conducted with two main aims: first, to examine the influence of starter films and the precracking condition on the initial mode I fracture toughness values; and second, to establish the definition of initial fracture toughness. Polyimide starter films stuck to the epoxy matrix, and caused unstable crack growth from starter films. Comparison of the tests with and without mode I precracks from starter films indicated that tests with precracks gave lower values of initial fracture toughness. The definition of initial fracture toughness values was discussed, based on the reproducibility. A 5% offset point was recommended as the initial fracture toughness from the RRT results. The influence of loading apparatus, data reduction methods, etc. was also discussed.