Analysis of shrinkage stresses arising during polymerization of orthodontic adhesive systems

IF 1.1 4区工程技术 Q4 POLYMER SCIENCE

Polimery Pub Date : 2023-08-21 DOI:10.14314/polimery.2023.5.4

K. Małkiewicz, M. Krasowski, Jakub Bartczak, Marta Radziejewska, K. Bociong

引用次数: 0

Abstract

The aim of the study was to evaluate the shrinkage stress during cross-linking of compositeorthodontic adhesive systems. The elastic-optical method was used for shrinkage stress analysis. Basedon the obtained results, basic statistics were determined, including averages and standard deviations.For the comparative analysis of the mean values, the Tukey HSD test was used at the significance levelα = 0.05. The average value of shrinkage stress during cross-linking ranged from 7.2 to 11.5 MPa.

查看原文本刊更多论文

正畸胶粘剂体系聚合过程中收缩应力的分析

本研究的目的是评估复合正畸粘接剂系统交联时的收缩应力。采用弹性光学法进行收缩应力分析。根据所得结果确定基本统计量，包括平均值和标准差。均数比较分析采用Tukey HSD检验，显著性水平α = 0.05。交联收缩应力的平均值为7.2 ~ 11.5 MPa。

本文章由计算机程序翻译，如有差异，请以英文原文为准。

求助全文

约1分钟内获得全文求助全文

来源期刊

Polimery Materials Science-Polymers and Plastics

CiteScore

2.90

自引率

6.20%

发文量

审稿时长

1 months

期刊介绍： The "Polimery" journal, of international circulation, is publishing peerreviewed scientific and technical research papers covering polymer science and technology in the field of polymers, rubbers, chemical fibres and paints. The range of topics covered are raw materials, polymer synthesis, processing and applications of polymers. Apart from scientific and technical research papers the monthly includes technical and commercial information such as reports from fairs and exhibitions as well as home, world and technical news. “Polimery "- an international journal covering the following topics: polymers, rubber, chemical fibres and paints. The Journal is addressed to scientists, managers and engineering staff of universities, Polish Academy of Sciences, R&D institutions, industry, specializing in polymer chemistry, physical chemistry, technology and processing. “Polimery” publishes original, reviewed research, scientific and technology papers in the field of polymer synthesis, analysis, technology and modification, processing, properties, applications and recycling.