Accelerated action of external sulfate and chloride to study corrosion of tensile steel in reinforced concrete

IF 1.1 4区 工程技术 Q3 CONSTRUCTION & BUILDING TECHNOLOGY
M. Silva, M. Cunha, A. Pinho-Ramos, B. S. D. Fonseca, F. Pinho
{"title":"Accelerated action of external sulfate and chloride to study corrosion of tensile steel in reinforced concrete","authors":"M. Silva, M. Cunha, A. Pinho-Ramos, B. S. D. Fonseca, F. Pinho","doi":"10.3989/MC.2017.10116","DOIUrl":null,"url":null,"abstract":"Corrosion of the reinforcing steel may cause significant loss of strength of reinforced concrete structures. The study focuses on accelerating such corrosion and examining the degradation of (i) the compressive strength of concrete due to sodium sulfate in a wet atmosphere; and (ii) the flexural strength by a solution of sodium sulfate and sodium chloride. Three types of concrete were used and different beam specimens were reinforced by steel rebars of different diameters (6, 8 and 10mm), part of the beams being pre-cracked. The concrete with least strength allowed higher sulfate penetration along the entire process and the compressive strength increased slightly, possibly due to lower porosity of concrete after contamination. The results of the flexural tests showed decrease of strength in all cases. Pre-cracked beams exhibited smaller influence of porosity of concrete. Beams with 6mm rebars showed the largest loss of strength due to the contamination and corrosion process","PeriodicalId":51113,"journal":{"name":"Materiales de Construccion","volume":"67 1","pages":"141"},"PeriodicalIF":1.1000,"publicationDate":"2017-10-05","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"4","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materiales de Construccion","FirstCategoryId":"5","ListUrlMain":"https://doi.org/10.3989/MC.2017.10116","RegionNum":4,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"CONSTRUCTION & BUILDING TECHNOLOGY","Score":null,"Total":0}
引用次数: 4

Abstract

Corrosion of the reinforcing steel may cause significant loss of strength of reinforced concrete structures. The study focuses on accelerating such corrosion and examining the degradation of (i) the compressive strength of concrete due to sodium sulfate in a wet atmosphere; and (ii) the flexural strength by a solution of sodium sulfate and sodium chloride. Three types of concrete were used and different beam specimens were reinforced by steel rebars of different diameters (6, 8 and 10mm), part of the beams being pre-cracked. The concrete with least strength allowed higher sulfate penetration along the entire process and the compressive strength increased slightly, possibly due to lower porosity of concrete after contamination. The results of the flexural tests showed decrease of strength in all cases. Pre-cracked beams exhibited smaller influence of porosity of concrete. Beams with 6mm rebars showed the largest loss of strength due to the contamination and corrosion process
外部硫酸盐和氯化物的加速作用研究钢筋混凝土中抗拉钢的腐蚀
钢筋的腐蚀可能导致钢筋混凝土结构强度的显著损失。该研究的重点是加速这种腐蚀,并检查以下方面的退化:(i)在潮湿的环境中,硫酸钠导致混凝土抗压强度下降;和(ii)通过硫酸钠和氯化钠溶液的弯曲强度。使用了三种类型的混凝土,不同的梁试样由不同直径(6、8和10mm)的钢筋加固,部分梁是预裂的。强度最低的混凝土在整个过程中允许更高的硫酸盐渗透,抗压强度略有增加,这可能是由于污染后混凝土的孔隙率较低。弯曲试验的结果表明,在所有情况下强度都有所下降。预裂梁受混凝土孔隙率的影响较小。具有6mm钢筋的梁由于污染和腐蚀过程而表现出最大的强度损失
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 求助全文
来源期刊
Materiales de Construccion
Materiales de Construccion 工程技术-材料科学:综合
CiteScore
3.20
自引率
9.50%
发文量
38
审稿时长
>12 weeks
期刊介绍: Materiales de Construcción is a quarterly, scientific Journal published in English, intended for researchers, plant technicians and other professionals engaged in the area of Construction, Materials Science and Technology. Scientific articles focus mainly on: - Physics and chemistry of the formation of cement and other binders. - Cement and concrete. Components (aggregate, admixtures, additions and similar). Behaviour and properties. - Durability and corrosion of other construction materials. - Restoration and conservation of the materials in heritage monuments. - Weathering and the deterioration of construction materials. - Use of industrial waste and by-products in construction. - Manufacture and properties of other construction materials, such as: gypsum/plaster, lime%2
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信