L. H. Da Silva, Laura Ajamil Rinaldi, D. Lazar, V. Ussui, R. Tango, R. Belli, U. Lohbauer, P. Cesar
{"title":"Development of Y-TZP/MWCNT-SiO2 nanocomposite for dental protheses.","authors":"L. H. Da Silva, Laura Ajamil Rinaldi, D. Lazar, V. Ussui, R. Tango, R. Belli, U. Lohbauer, P. Cesar","doi":"10.2139/ssrn.4388790","DOIUrl":null,"url":null,"abstract":"Y-TZP/MWCNT-SiO2 nanocomposite was synthesized by co-precipitation and hydrothermal treatment methods. After the characterization of the MWCNT-SiO2 powder, specimens were obtained from the synthesized material Y-TZP/MWCNT-SiO2 by uniaxial pressing for a second characterization and later comparison of its optical and mechanical properties with the conventional Y-TZP. The MWCNT-SiO2 was presented in bundles of carbon nanotubes coated by silica (mean length: 5.10 ± 1.34 μm /D90: 6.9 μm). The composite manufactured was opaque (contrast ratio: 0.9929 ± 0.0012) and had a white color with a slightly difference from the conventional Y-TZP (ΔE00: 4.4 ± 2.2) color. The mechanical properties of Y-TZP/MWCNT-SiO2: vickers hardness (10.14 ± 1.27 GPa; p = 0.25) and fracture toughness (4.98 ± 0.30 MPa m1/2; p = 0.39), showed no significant difference from the conventional Y-TZP (hardness: 8.87 ± 0.89; fracture toughness: 4.98 ± 0.30 MPa m1/2). However, for flexural strength (p = 0.003), a lower value was obtained for Y-TZP/MWCNT-SiO2 (299.4 ± 30.5 MPa) when compared to the control Y-TZP (623.7 ± 108.8 MPa). The manufactured Y-TZP/MWCNT-SiO2 composite presented satisfactory optical properties, however the co-precipitation and hydrothermal treatment methods need to be optimized to avoid the formation of porosities and strong agglomerates, both from Y-TZP particles and MWCNT-SiO2 bundles, which lead to a significant decrease in the material flexural strength.","PeriodicalId":94117,"journal":{"name":"Journal of the mechanical behavior of biomedical materials","volume":"143 1","pages":"105888"},"PeriodicalIF":0.0000,"publicationDate":"2023-05-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of the mechanical behavior of biomedical materials","FirstCategoryId":"0","ListUrlMain":"https://doi.org/10.2139/ssrn.4388790","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
Y-TZP/MWCNT-SiO2 nanocomposite was synthesized by co-precipitation and hydrothermal treatment methods. After the characterization of the MWCNT-SiO2 powder, specimens were obtained from the synthesized material Y-TZP/MWCNT-SiO2 by uniaxial pressing for a second characterization and later comparison of its optical and mechanical properties with the conventional Y-TZP. The MWCNT-SiO2 was presented in bundles of carbon nanotubes coated by silica (mean length: 5.10 ± 1.34 μm /D90: 6.9 μm). The composite manufactured was opaque (contrast ratio: 0.9929 ± 0.0012) and had a white color with a slightly difference from the conventional Y-TZP (ΔE00: 4.4 ± 2.2) color. The mechanical properties of Y-TZP/MWCNT-SiO2: vickers hardness (10.14 ± 1.27 GPa; p = 0.25) and fracture toughness (4.98 ± 0.30 MPa m1/2; p = 0.39), showed no significant difference from the conventional Y-TZP (hardness: 8.87 ± 0.89; fracture toughness: 4.98 ± 0.30 MPa m1/2). However, for flexural strength (p = 0.003), a lower value was obtained for Y-TZP/MWCNT-SiO2 (299.4 ± 30.5 MPa) when compared to the control Y-TZP (623.7 ± 108.8 MPa). The manufactured Y-TZP/MWCNT-SiO2 composite presented satisfactory optical properties, however the co-precipitation and hydrothermal treatment methods need to be optimized to avoid the formation of porosities and strong agglomerates, both from Y-TZP particles and MWCNT-SiO2 bundles, which lead to a significant decrease in the material flexural strength.