Jianfa Wang, Zhengzhou Gu, Jie Zhao, Susu Zhang, Peiyao Li, Chao Meng, J. Sui, Xiaoyi Zhang, Shaokai Hu, Jiaying Pan, Junyi Li
{"title":"Aging behavior of three-proof polyurethane coatings under UV radiation","authors":"Jianfa Wang, Zhengzhou Gu, Jie Zhao, Susu Zhang, Peiyao Li, Chao Meng, J. Sui, Xiaoyi Zhang, Shaokai Hu, Jiaying Pan, Junyi Li","doi":"10.14314/polimery.2022.9.4","DOIUrl":null,"url":null,"abstract":"The influence of UV radiation on the physical and mechanical properties of polyurethane resins and three-proof polyurethane coatings was examined. Changes of mechanical properties and the gloss of resins and coatings were determined. The structure of materials was confirmed using scanning microscopy SEM and Fourier transform infrared spectroscopy FTIR; thermogravimetric TGA and DTG studies were also performed. It turned out that the gloss of finished protective coatings was worse than the gloss of individual resins, and aging significantly lowered these values (from 81.3° to 8.9° in case of resins and from 61.1° to 2.8° in case of coatings after 1200 hours of irradiation). Tensile strength of resins decreased constantly during aging while their elongation at break decreased than increased reaching minimum at exposure time of 100 hours. In case of coatings, both tensile strength and elongation at break firstly decreased than increased reaching minimum at exposure time of 800 hours; after long exposure time, more than 1200 hours, these properties decreased again.","PeriodicalId":20319,"journal":{"name":"Polimery","volume":" ","pages":""},"PeriodicalIF":1.1000,"publicationDate":"2022-09-29","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Polimery","FirstCategoryId":"5","ListUrlMain":"https://doi.org/10.14314/polimery.2022.9.4","RegionNum":4,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"POLYMER SCIENCE","Score":null,"Total":0}
引用次数: 0
Abstract
The influence of UV radiation on the physical and mechanical properties of polyurethane resins and three-proof polyurethane coatings was examined. Changes of mechanical properties and the gloss of resins and coatings were determined. The structure of materials was confirmed using scanning microscopy SEM and Fourier transform infrared spectroscopy FTIR; thermogravimetric TGA and DTG studies were also performed. It turned out that the gloss of finished protective coatings was worse than the gloss of individual resins, and aging significantly lowered these values (from 81.3° to 8.9° in case of resins and from 61.1° to 2.8° in case of coatings after 1200 hours of irradiation). Tensile strength of resins decreased constantly during aging while their elongation at break decreased than increased reaching minimum at exposure time of 100 hours. In case of coatings, both tensile strength and elongation at break firstly decreased than increased reaching minimum at exposure time of 800 hours; after long exposure time, more than 1200 hours, these properties decreased again.
期刊介绍:
The "Polimery" journal, of international circulation, is publishing peerreviewed scientific and technical research papers covering polymer science and technology in the field of polymers, rubbers, chemical fibres and paints. The range of topics covered are raw materials, polymer synthesis, processing and applications of polymers. Apart from scientific and technical research papers the monthly includes technical and commercial information such as reports from fairs and exhibitions as well as home, world and technical news.
“Polimery "- an international journal covering the following topics: polymers, rubber, chemical fibres and paints.
The Journal is addressed to scientists, managers and engineering staff of universities, Polish Academy of Sciences, R&D institutions, industry, specializing in polymer chemistry, physical chemistry, technology and processing. “Polimery” publishes original, reviewed research, scientific and technology papers in the field of polymer synthesis, analysis, technology and modification, processing, properties, applications and recycling.