Next-Generation Electrode Materials: La/Ce Doping for Superior Anodic Oxidation

Abstract

In this study, the characterization, optimization and effect of model compound Reactive Black 5 (RB5) dye on the process performance of lanthanum (La) and cerium (Ce) doped iridium-ruthenium (Ir-Ru) mixed metal oxide (MMO) electrodes were investigated. The electrodes had varying La and Ce doping levels at 5%, 10% and 20% concentrations and were coated by thermal decomposition technique. In addition, a mixed La/Ce electrode was prepared with 10% Ce and 10% La. This study focused on understanding the effects of La and Ce doping, pH, conductivity and concentration on the electrochemical degradation process. The experiments were conducted over various pH values ​​(3, 5, 7 and 9), dye concentrations (50, 100, 300 and 500 ppm), current densities (100, 200, 350 and 600 A.m-²) and conductivities (1500, 3500, 5500 and 10000 µS.cm⁻¹). It was found that the newly developed electrode doped with 10% Ce and 10% La showed the most efficient results. This study provides insights into optimizing the operational parameters for effective electrochemical process with the novel La/Ce doped MMO electrodes.