Phase Evolution in Mn1.6Zn0.2Ni0.6Mg0.2Al0.4O4 High-Entropy Oxide Films by Heat Treatment.

Abstract

In this work, Mn-Zn-Ni-Mg-Al multi-layer films were annealed in air at different temperatures to form spinel-structured Mn_1.6Zn_0.2Ni_0.6Mg_0.2Al_0.4O₄ high-entropy oxide films. X-ray diffraction results demonstrate that the films possess a polycrystalline spinel phase as well as impurity phases: when annealed at 650 °C and 750 °C, MnO₂ and Al₂O₃ impurity phases exist; at 950 °C, an Al₂O₃ impurity phase exists. Only at 850 °C does a pure spinel phase exist. However, the film at 750 °C exhibits the best conductive behavior, which indicates that the impurity phases may not have to be removed to maintain the best electrical properties of the film.