Effects of glutathione and potassium iodide on silver diamine fluoride application on remineralisation and colour change in dentine caries of primary teeth: an in vitro study.

Abstract

Purpose: The aim of this study is to compare the effect of GSH (reduced glutathione) and KI (potassium iodide) on SDF (silver diamine fluoride) discolouration and dentine remineralisation.

Methods: Sixteen primary molars were utilised, yielding 4 dentine specimens each. Three specimens per tooth were allocated: one as a control and the others to experimental groups. Initial microhardness measurements were taken from one remaining dentine specimen per tooth. Subsequently, all groups underwent exposure to a demineralisation solution. Colorimetry assessed specimen colour, and post-second microhardness measurements on demineralised specimens, treatments were administered as follows: group 1 (control, n = 16): 38% SDF, group 2 (n = 16): 38% SDF followed by KI, group 3 (n = 16): 38% SDF with 5% GSH added by weight. Following pH cycling across all groups, colorimetry reassessed 48 dentine specimens. Final microhardness measurements ensued, followed by statistical analysis. Normality was checked via Shapiro-Wilk, and homogeneity via Levene's test. Independent samples t test compared normally distributed groups; Mann-Whitney U compared non-normally distributed groups. ANOVA compared means of normally distributed groups, and Kruskal-Wallis for non-normally distributed ones. Repeated measures ANOVA compared dependent groups with normal distribution, and Friedman test for non-normal. Post hoc Bonferroni analyses identified significant differences. IBM SPSS 25 was used to conduct analyses.

Results: The mean ΔE* values for SDF and SDF + GSH groups were significantly higher than those of the SDF + KI group (p < 0.05). Significant differences in L* values during final colour measurement were noted between the SDF + KI group and both SDF and SDF + GSH groups (p < 0.05). Although mean remineralisation microhardness measurements were higher than mean demineralisation microhardness measurements in all groups, statistical significance was observed only in the SDF and SDF + KI groups (p < 0.05).

Conclusion: The study found that the addition of 5% GSH by weight to SDF does not significantly affect discolouration. Moreover, the addition of 5% GSH to the SDF solution may have a minor impact on the remineralisation potential of SDF. The application of KI after SDF reduces discolouration and does not affect the expected remineralisation process.