Influence of microstructure on optical properties of CAD-CAM lithium disilicate glass-ceramics

Abstract

Objectives

To evaluate the influence of microstructure and chemical composition on the optical properties of CAD-CAM lithium disilicate glass-ceramics.

Methods

Samples (n = 5; 1.0 mm thickness) of shades A1, A2, and A3 were fabricated from CAD-CAM ceramic blocks (Ivoclar Vivadent): IPS e.max® CAD LT (emLT) and HT (emHT). Samples were polished to 1.0 ± 0.01 mm in thickness. The optical properties (R- reflectance; T- transmittance; ${\mu }_s^{\prime }$- reduced scattering and ${\mu }_a$- absorption coefficients) from the post-crystallized samples were determined using the inverse adding-doubling (IAD) method based on integrating-sphere measurements. Additionally, scanning electron microscopy (SEM) and X-ray diffraction (XRD) techniques were used to evaluate the microstructural properties. Energy-dispersive X-ray (EDX) was employed to analyze the chemical composition. The chemical and structural characterization were performed before and after crystallization of the ceramic samples.

Results

emLT showed higher values of ${\mu }_s^{\prime }$and lower values of ${\mu }_a$ and T than emHT for each shade in all wavelengths (p < 0.003). Considering T for emHT, there were no statistical differences for shades A1 and A2 at 488 nm and 514.5 nm (p > 0.003) and shades A1 and A3 at 457.9 nm (p > 0.003). emLT showed particle length ranging from 0.74 to 2.78 µm (mean = 1.57 µm and RF-relative frequency = 28 %) and particle width ranging from 0.21 to 0.74 µm (mean = 0.30 µm and RF = 31 %). emHT showed particle length ranging from 0.83 to 3.08 µm (mean = 1.86 µm and RF = 21 %) and particle width ranging from 0.24 to 1.12 µm (mean = 0.56 µm and RF = 28 %). In comparison with emHT, emLT showed greater vol% for C, K, and Zr and lower vol% for O and Al.

Significance

The optical properties of CAD-CAM lithium disilicate glass-ceramics are influenced by the chemical composition and, consequently, by the material microstructure.