Process Optimization of Ni60A Coating Preparation by Plasma Spraying-Cladding Technique

Abstract

Ni60A spraying-cladding coatings were innovatively prepared on the surface of the Q235 steel substrate by plasma spraying-cladding technique. Ni60A powder with a particle size of 30 μm was further selected as the optimum spraying-cladding powder based on preliminary numerical simulation. The spraying-cladding distanceØ was optimized, and the optimum distance was determined as 18 and 16 mm, respectively, for the internal feeding process and external feeding process. The microhardness of the spraying-cladding coating could reach 875.6 HV during the internal feeding process at a spraying-cladding distance of 18 mm, and reach 791.6 HV during the external feeding process at a spraying-cladding distance of 16 mm. Meanwhile, the thermal effect of the plasma spraying-cladding technique on the Q235 steel substrate was less.