{"title":"Enhancement the physical properties of V2O5/Ni0.1Fe2.9O4 nanocomposite","authors":"Rania Ramadan","doi":"10.1007/s41779-024-01051-5","DOIUrl":null,"url":null,"abstract":"<div><p>Nanocomposite containing vanadium oxide (V<sub>2</sub>O<sub>5</sub>) and magnetite (Fe<sub>3</sub>O<sub>4</sub>) doped with nickel (Ni) ion were synthesized according to the formula of Ni<sub>0.1</sub>Fe<sub>2.9</sub>O<sub>4</sub> /V<sub>2</sub>O<sub>5</sub>. The obtained composition was characterized by XRD, FTIR, FESEM. The FESEM micrograph shows that the existence of two different phases related to V<sub>2</sub>O<sub>5</sub> and Ni-Magnetite. Moreover,the roughness parameters have values of 281, 85 and 385nm for roughness average R<sub>a</sub>, root mean square roughness R<sub>q,</sub> Maximum height of roughness R<sub>T</sub> respectively. Moreover, the magnetic behavior of the sample was studied, and we found that by adding V<sub>2</sub>O<sub>5</sub> to Ni dopped magnetite, the curie temperature value was lowered from 750 <sup>o</sup>C to 625 <sup>o</sup>C. The activation energy was calculated and found to be 0.22 eV and 0.08 eV for 1000 Hz and 3MHz respectively.</p></div>","PeriodicalId":673,"journal":{"name":"Journal of the Australian Ceramic Society","volume":"60 5","pages":"1437 - 1446"},"PeriodicalIF":1.8000,"publicationDate":"2024-07-15","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://link.springer.com/content/pdf/10.1007/s41779-024-01051-5.pdf","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of the Australian Ceramic Society","FirstCategoryId":"88","ListUrlMain":"https://link.springer.com/article/10.1007/s41779-024-01051-5","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"MATERIALS SCIENCE, CERAMICS","Score":null,"Total":0}
引用次数: 0
Abstract
Nanocomposite containing vanadium oxide (V2O5) and magnetite (Fe3O4) doped with nickel (Ni) ion were synthesized according to the formula of Ni0.1Fe2.9O4 /V2O5. The obtained composition was characterized by XRD, FTIR, FESEM. The FESEM micrograph shows that the existence of two different phases related to V2O5 and Ni-Magnetite. Moreover,the roughness parameters have values of 281, 85 and 385nm for roughness average Ra, root mean square roughness Rq, Maximum height of roughness RT respectively. Moreover, the magnetic behavior of the sample was studied, and we found that by adding V2O5 to Ni dopped magnetite, the curie temperature value was lowered from 750 oC to 625 oC. The activation energy was calculated and found to be 0.22 eV and 0.08 eV for 1000 Hz and 3MHz respectively.
期刊介绍：
Publishes high quality research and technical papers in all areas of ceramic and related materials
Spans the broad and growing fields of ceramic technology, material science and bioceramics
Chronicles new advances in ceramic materials, manufacturing processes and applications
Journal of the Australian Ceramic Society since 1965
Professional language editing service is available through our affiliates Nature Research Editing Service and American Journal Experts at the author''s cost and does not guarantee that the manuscript will be reviewed or accepted
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号