Achieving property enhancements in dental resin composites via reduced concentrations of camphorquinone within a ternary initiator system

Abstract

Objectives

The study aimed to assess the impact of diphenyliodonium hexafluorophosphate (DPI) on the physicochemical properties of experimental resin composites (ECRs) featuring reduced concentrations of camphorquinone (CQ)/amine.

Methods

Five concentrations of CQ (0.125, 0.25, 0.5, 0.75, and 1 mol%) with dimethylaminoethyl amine benzoate (EDAB) in a 1:2 mol% ratio (CQ:EDAB) were incorporated into a 50:50 mass% monomer blend of bisphenol glycidyl methacrylate (BisGMA) and triethyleneglycol dimethacrylate (TEGDMA). An additional 5 groups with the same CQ:EDAB concentrations had 0.5 mol% DPI added. Each resin group contained 60 wt% of 0.7 µm barium-alumino-silicate glass. Light transmission (n = 3), real-time degree of polymerization (n = 3), temperature change during polymerization (n = 5), polymerization shrinkage strain (n = 3), flexural strength, and modulus (n = 12), as well as water sorption and solubility (n = 5), were evaluated. Data were analyzed using two-way ANOVA and Tukey's post-hoc test (α = 0.05).

Results

Light transmission was reduced in groups containing 0.125 and 0.25 mol% of CQ without DPI. DPI increased temperature, degree and rate of polymerization, despite the reduction in CQ/amine concentration. Additionally, there was an increase in polymerization shrinkage strain, flexural strength and modulus, and a reduction in water sorption and solubility in ECRs with DPI, even with lower concentrations of CQ/EDAB.

Significance

DPI improved the assessed properties of composites across various concentrations of CQ/EDAB, showing the benefit of reducing the quantity of CQ used without compromising the properties and curing of the resin composites.