Optimasi Sintesis Nanopartikel ZnO dengan Metode Hidrotermal

Abstract

ZnO is an inorganic material that has many benefits, one of which is in the pharmaceutical field. So far, the synthesis of inorganic materials has been carried out using high temperatures. Research was carried out to synthesize ZnO using hydrothermal at 180°C for 24 hours then burned at temperatures of 300, 600, and 900°C for 6 hours. The compound resulting from synthesis at 180°C was obtained by the compound [Zn(urea)3](NO3)2 which decomposed into ZnO nanoparticle compounds at 300°C to 900°C. ZnO synthesized at temperatures of 300, 600, and 900°C has a hexagonal structure, space group P63/m with lattice parameters a=b= 3.25 Å and c= 5.21 Å and ? = ? = 90° and ? = 120°. The synthesized ZnO has a nanoparticle size in the range of 172-455 nm. Keywords:          ZnO, hydrothermal, synthesis, nanoparticle, hexagonal structure   Abstrak ZnO merupakan material anorganik yang memiliki banyak manfaat, salah satunya dalam bidang farmasi. Selama ini sintesis material anorganik dilakukan menggunakan suhu yang tinggi. Penelitian dilakukan untuk mensintesis material ZnO pada suhu rendah. Metode sintesis material ZnO dilakukan dengan menggunakan hidrotermal pada suhu 180°C selama 24 jam kemudian dibakar pada suhu 300, 600, dan 900°C selama 6 jam. Senyawa hasil sintesis pada 180°C diperoleh senyawa [Zn(urea)3](NO3)2 yang terurai menjadi senyawa nanopartikel ZnO pada 300°C hingga 900°C. ZnO hasil sintesis pada suhu 300, 600, dan 900°C memiliki struktur heksagonal, grup ruang P63/m dengan parameter kisi a=b= 3,25 Å dan c= 5,21 Å serta memiliki sudut ? = ? = 90° dan ? = 120°. ZnO hasil sintesis memiliki ukuran nanopartikel dengan rentang 172-455 nm. Kata Kunci:         ZnO, hidrotermal, sintesis, nanopartikel, struktur heksagonal