Cr-doped Mesoporous M1 Phase MoVTeNbOx Catalyze Selective Oxidation of Propane to Acrylic Acid

Abstract

In this work, MoVTeNbO_x catalysts was doped with Cr by using spray drying method. The effect of Cr doping on the crystalline phase, physicochemical properties, and catalytic performance of selective oxidation of propane to acrylic acid of MoVTeNbO_x was investigated. The results showed that the samples as-prepared by spray drying method present unique spherical morphology stacked by rod particles. In addition, Cr doping induced a change in the mesopore structure formed by rod stacking, reducing the pore radius of the catalysts from 5-10 nm to 2-4 nm. Meanwhile, Cr doping dramatically reduced the average particle size of MoVTeNbO_x catalysts, decreasing the rod cross-section diameter of catalysts from 234.21 to 134.96 nm and the rod length from 1.096 μm to 485.71 nm, which significantly increased the amount of (001) active crystalline plane. Moreover, an appropriate amount of Cr doping increased the number of reducible species in the catalyst and reduced its acidity. At the same time, the surface V⁵⁺ content of the catalyst was increased from 35.8% to 72.6%. Cr-doped MoVTeNbO_x with mesoporous structure showed excellent performance in catalyzing selective oxidation of propane to acrylic acid reaction. Among them, S-3 sample (V: Cr = 1:0.015) increased the selectivity and yield to acrylic acid from 67.5% to 84.3% and from 26.4% to 43.2%, respectively, at reaction temperature of 380 °C.