{"title":"Copper micromesh-based lightweight transparent conductor with short response time for wearable heaters","authors":"Han-Jung Kim, Yoonkap Kim","doi":"10.1186/s40486-021-00132-5","DOIUrl":null,"url":null,"abstract":"<div><p>Thickness-controlled transparent conducting films (TCFs) were fabricated by transfer printing a 100 nm thick Cu micromesh structure onto poly(vinyl alcohol) (PVA) substrates of different thicknesses (~ 50, ~ 80, and ~ 120 μm) to develop a lightweight transparent wearable heater with short response time. The Cu mesh-based TCF fabricated on a ~ 50 µm thick PVA substrate exhibited excellent optical and electrical properties with a light transmittance of 86.7% at 550 nm, sheet resistance of ~ 10.8 Ω/sq, and figure-of-merit of approximately 236, which are comparable to commercial indium tin oxide film-based transparent conductors. The remarkable flexibility of the Cu mesh-based TCF was demonstrated through cyclic mechanical bending tests. In addition, the Cu mesh-based TCF with ~ 50 μm thick PVA substrate demonstrated a fast Joule heating performance with a thermal response time of ~ 18.0 s and a ramping rate of ~ 3.0 ℃/s under a driving voltage of 2.5 V. Lastly, the reliable response and recovery characteristics of the Cu mesh/PVA film-based transparent heater were confirmed through the cyclic power test. We believe that the results of this study is useful in the development of flexible transparent heaters, including lightweight deicing/defogging films, wearable sensors/actuators, and medical thermotherapy pads.</p></div>","PeriodicalId":704,"journal":{"name":"Micro and Nano Systems Letters","volume":null,"pages":null},"PeriodicalIF":4.7000,"publicationDate":"2021-10-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://mnsl-journal.springeropen.com/counter/pdf/10.1186/s40486-021-00132-5","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Micro and Nano Systems Letters","FirstCategoryId":"1085","ListUrlMain":"https://link.springer.com/article/10.1186/s40486-021-00132-5","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"NANOSCIENCE & NANOTECHNOLOGY","Score":null,"Total":0}
引用次数: 0
Abstract
Thickness-controlled transparent conducting films (TCFs) were fabricated by transfer printing a 100 nm thick Cu micromesh structure onto poly(vinyl alcohol) (PVA) substrates of different thicknesses (~ 50, ~ 80, and ~ 120 μm) to develop a lightweight transparent wearable heater with short response time. The Cu mesh-based TCF fabricated on a ~ 50 µm thick PVA substrate exhibited excellent optical and electrical properties with a light transmittance of 86.7% at 550 nm, sheet resistance of ~ 10.8 Ω/sq, and figure-of-merit of approximately 236, which are comparable to commercial indium tin oxide film-based transparent conductors. The remarkable flexibility of the Cu mesh-based TCF was demonstrated through cyclic mechanical bending tests. In addition, the Cu mesh-based TCF with ~ 50 μm thick PVA substrate demonstrated a fast Joule heating performance with a thermal response time of ~ 18.0 s and a ramping rate of ~ 3.0 ℃/s under a driving voltage of 2.5 V. Lastly, the reliable response and recovery characteristics of the Cu mesh/PVA film-based transparent heater were confirmed through the cyclic power test. We believe that the results of this study is useful in the development of flexible transparent heaters, including lightweight deicing/defogging films, wearable sensors/actuators, and medical thermotherapy pads.