Wear and corrosion resistance of zinc-oxide and zirconium-oxide coated WE43 magnesium alloy

IF 2.4 3区 材料科学 Q3 MATERIALS SCIENCE, COATINGS & FILMS
Canser Gül, Hülya Durmuş, Sevda Albayrak, Nilay Çömez
{"title":"Wear and corrosion resistance of zinc-oxide and zirconium-oxide coated WE43 magnesium alloy","authors":"Canser Gül, Hülya Durmuş, Sevda Albayrak, Nilay Çömez","doi":"10.1116/6.0002894","DOIUrl":null,"url":null,"abstract":"Magnesium alloy, which draws attention with its lightness and high specific strength, is frequently preferred due to its advantages. However, it is necessary to improve the wear and corrosion properties in order to develop the areas of use in the automotive, aircraft, and space industries. For this purpose, after the surface preparation of the main material WE43 Mg alloy, ZnO and ZrO2 coatings were made and characterized in this study. The surface morphology and structural and chemical properties of the samples were investigated using profilometry, contact angle tests, scanning electron microscopy, and x-ray diffraction. Corrosion tests have been carried out. In order to determine the wear performance of the samples, the wear-related volume losses were measured and the friction coefficients were compared. Layers with 2–6 μm coating thickness were obtained homogeneously on the polished and sandblasted sample surfaces. It was determined that the coating layers grew in the form of columns and did not contain capillary cracks. As a result of the study, it was observed that the ZnO-coated samples had the highest wear and corrosion resistance, and the wear and corrosion resistance of the coatings and magnesium alloy substrates improved.","PeriodicalId":17490,"journal":{"name":"Journal of Vacuum Science & Technology A","volume":null,"pages":null},"PeriodicalIF":2.4000,"publicationDate":"2023-10-04","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Vacuum Science & Technology A","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1116/6.0002894","RegionNum":3,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, COATINGS & FILMS","Score":null,"Total":0}
引用次数: 0

Abstract

Magnesium alloy, which draws attention with its lightness and high specific strength, is frequently preferred due to its advantages. However, it is necessary to improve the wear and corrosion properties in order to develop the areas of use in the automotive, aircraft, and space industries. For this purpose, after the surface preparation of the main material WE43 Mg alloy, ZnO and ZrO2 coatings were made and characterized in this study. The surface morphology and structural and chemical properties of the samples were investigated using profilometry, contact angle tests, scanning electron microscopy, and x-ray diffraction. Corrosion tests have been carried out. In order to determine the wear performance of the samples, the wear-related volume losses were measured and the friction coefficients were compared. Layers with 2–6 μm coating thickness were obtained homogeneously on the polished and sandblasted sample surfaces. It was determined that the coating layers grew in the form of columns and did not contain capillary cracks. As a result of the study, it was observed that the ZnO-coated samples had the highest wear and corrosion resistance, and the wear and corrosion resistance of the coatings and magnesium alloy substrates improved.
氧化锌和氧化锆包覆WE43镁合金的耐磨损和耐腐蚀性能
镁合金以其重量轻、比强度高的特点受到人们的关注,因其优点而成为人们的首选。然而,为了在汽车、飞机和航天工业中发展其应用领域,有必要改善其磨损和腐蚀性能。为此,本研究在对主要材料WE43镁合金进行表面制备后,制备了ZnO和ZrO2涂层并对其进行了表征。利用轮廓术、接触角测试、扫描电子显微镜和x射线衍射对样品的表面形貌、结构和化学性质进行了研究。进行了腐蚀试验。为了确定样品的磨损性能,测量了与磨损相关的体积损失,并比较了摩擦系数。在抛光和喷砂样品表面均可获得2 ~ 6 μm厚度的涂层。结果表明,涂层呈柱状生长,不含毛细裂纹。结果表明,zno涂层样品具有最高的耐磨损和耐腐蚀性能,涂层和镁合金基体的耐磨损和耐腐蚀性能均有提高。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 求助全文
来源期刊
Journal of Vacuum Science & Technology A
Journal of Vacuum Science & Technology A 工程技术-材料科学:膜
CiteScore
5.10
自引率
10.30%
发文量
247
审稿时长
2.1 months
期刊介绍: Journal of Vacuum Science & Technology A publishes reports of original research, letters, and review articles that focus on fundamental scientific understanding of interfaces, surfaces, plasmas and thin films and on using this understanding to advance the state-of-the-art in various technological applications.
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信