Electrical surface resistivity of organic coating resin in arc-decomposed SF6 gas

Abstract

The electrical surface resistivity of polymer base coating was investigated in arc-decomposed SF6 gas. The thickness of more than 100 mum was found necessary to prevent the adverse effect of arc-decomposed SF6 gas, which penetrated the coated film and deteriorated the insulation properties of the base material. The effect of the cure condition of the coated film was also investigated by using differential scanning calorimeter (DSC). An endothermic peak due to uncured agent, which reduced the surface resistivity in arc-decomposed SF6 gas, was observed.